A study has been conducted to determine the cyclic and static thermal stability fo Ti-44Al-11Nb alloy in air in a range of temperature from 900 to 1000 degree. Weight gain method shows that the static oxidation rates are higher than cyclic oxidation rates under identical experimental conditions at a given temperature. The oxide layer at the surface peretrates the base metal in a direction parallel to the lamellae of the two phases, alft sub 2 and lambda, confirmed by scanning electron micrographs. THe thermal stability fo up to 168 hours indicates that there are phase transformatios taking placed afecting the microstructures in such a way that large amount of dislocation activities are involved.