Application of Barkhausen Noise Residual Stress Measurement Technique to Solve Cracking Problem in Diesel Engine Cylinder Heads

摘要

The problem of valve bridge crackign was observed in gray iron cylinder heads during expensive 1000 hours thermal fatigue test. After elimination of various reasns in course of failure analysis, it was suspected that residual stresses in the component are responsible for this failure.