Investigation of a PEM Water Electrolyzer Based on a Sulfonated Polysulfone Membrane

摘要

A sulfonated polysulfone (SPSf) membrane was prepared and used as polymer electrolyte in water electrolysis cell. The behaviour of SPSf in PEMWE was investigated by polarization, electrochemical impedance spectroscopy and chrono-amperometry. The performance was compared to a commercial Nafion 115 membrane. A low series resistance of 0.13 Ω·cm~2 was measured for the SPSf membrane at 80°C under water electrolysis. At the same potential value, 1.8 V, the current density values in the polarization curves were 1.29 A·cm~(-2) and 1.08 A·cm~(-2) for the cells with Nafion and SPSf membrane, respectively. During a chrono-amperometric measurement, the current density remained constant throughout the test, indicating a suitable stability of the SPSf based cell. The good performance, low cost and excellent lifetime stability of SPSf make this polymer a promising solid electrolyte for the application in PEM electrolyzers.