Full Scale SSC Testing of High Hardness 4130 Steel Riser P-line Weldments

摘要

American Petroleum Institute (API) standard 16C, Choke and Kill System, requires that peripheral lines (P-lines) meet the hardness requirements of NACE MR0175/ISO15156-2. This means a maximum hardness of 22HRC for low alloy steels. Further, NACE MR0175/ISO15156-2 allows downhole casing, tubing and tubular components made of AISI 41xx steels, quenched and tempered in tubular form, to have a hardness of 26HRC, but each heat should be qualified by Sulfide Stress Cracking (SSC) testing in accordance with NACE MR0175/ISO15156-2 Clause B.1 using the tensile test. During production of AISI 4130 Q&T drilling riser choke and kill lines weld cap hardness over 237HB/22HRC was experienced. This article describes Capcis HSE OTI 95-635 full pipe ring sour corrosion tests on high hardness AISI 4130 Q&T P-line pipe and weldments. In the full pipe ring tests, welded pipes were loaded by squeezing up to a Hoop stress of 552MPa (SMYS) in the outer surface. Test solution was the NACE TM0177 solution A, with H_2S partial pressure of 0.01, 0.1 and 1.0 bar (1, 10 and 100 kPa), respectively. Pipes and welds (weld cap and heat affected zone) with hardness that ranged from 230HV_(10) to 357HVio did not show any signs of hydrogen induced sulfide stress cracking after the 30 days exposure. Test procedure and an overview of actual pipe and HAZ hardness variations are presented.