ANALYSE AND CONTROL RESEARCH ABOUT THE CAUSE OF SHAPE DEFECTS ON HOT-ROLLED STRIP STEEL

摘要

Strip shape defects, especially the crown problem, once appeared in the production of hot-rolled strip steel in SG Company. The macroscopic characteristic is the thickness difference occurred between the center and edge cross section of hot-rolled plate. Morphological characteristics and forming reasons can be got by analyzing roll wear. Research shows that the main reason for the formation of crown is excessive attrition of work roll in later period, which leading to smaller roll shape. Therefore, shape defects have been effectively controlled after introducing CVC roll contour technology to optimize roll shape. Quality qualified rate of strip shape of hot-rolled strip steel is more than 99.6% percent, and it has been successfully put into application of hotrolling mill.