STUDY ON THE IMPROVEMENTS OF REDUCTION SWELLABILITY AND LOW TEMPERATURE REDUCTION DISINTEGRATION OF VANADIUM-TITANIUM MAGNETITE OXIDIZED PELLETS

摘要

Reduction swellability index (RSI) and low temperature reduction disintegration index (RDI) of vanadium-titanium magnetite oxidized pellets are harmful to the processing of ironmaking, for example, causing serious gas permeability, decreased yield, higher coke ratio and more furnace dust. Thus, the improvements of RSI and RDI of vanadium-titanium magnetite oxidized pellets were investigated in this paper, including the pretreatment of raw material, additives of dolomite or boric acid, pellets treated in chloride solution and so on. The results showed that damp milling as pretreatment and boric acid added in pelletizing were conducive to the RSI which decreased 5% and 7% respectively, while they were not efficient enough in improving RDI. Dolomite was efficient in improving RSI, but had negative effect on RDI. There was no evidence to show that RSI and RDI would be improved when pellets were treated in chloride solution. Pursuing this further, the mechanism of those improvements were investigated.