ISOTHERMAL BAINITE TRANSFORMATION OF CR5 STEEL UNDER PULSED CURRENT AND PULSED MAGNETIC FIELD TREATMENT

摘要

Pulsed current and pulsed magnetic field have been applied to the bainite transformation of Cr5 steel. Three groups of experiments were conducted. In the first group, ordinary resistance furnace was used for heat treatment. The Cr5 specimens were rapidly heated up to austenitization temperature 940 °C, held for 20 min, air cooled to bainite transformation temperature 350 °C, held for 10, 20, or 40 min and then air cooled to room temperature. The second and the third group shared the same temperature-time curve with that of the first group, but their heat resources came from the Joule heat produced by pulsed current. 1.5 T pulsed magnetic field was exerted on the third group specimens when they were held at 350 °C, but the second group specimens did not undergo the treatment of magnetic field. It was found that both pulsed current and pulsed magnetic field obviously retarded the bainite transformation. The phenomena were discussed in terms of literature results.