The Effect of Aluminum Addition to the ESR Process Slag on IN718 Superalloy Characteristics

摘要

This research was conducted to study the changes of microstructure, chemical composition and mechanical properties of IN718 superalloy after adding aluminum to the ESR process slag. The experiments were performed in VIM and ESR furnaces. The results showed adding 1.5 percent aluminum to the slag increase lave phase in the IN718 samples from 0.34 percent in the base sample to 3.0 percent. It also indicated that the more increase of aluminum in slag cause decrease in the aluminum absorb yield in the superalloy it is observed that increasing aluminum from 0.7 to 1.1 and then to 1.5 percent caused a decrease of absorb from 91.4 to 76.3 and 74.6 percent respectively due to increasing of aluminum oxidation. According to the results, tensile strength increased and ductility declined in the IN718 samples mainly because of rising the amount of γ' volume fraction.