RESEARCH ON OXIDATION KINETICS OF SPHC STEEL AT 500~900°C

摘要

Oxidation Kinetics of SPHC was analyzed by TGA, and the curve of oxidation weight gain with different temperature was acquired. It is found that, when the oxidation temperature is between 500°C and 600°C, all the curves are linear; when the oxidation temperature is above 700°C, the curves are close to parabolic. At the temperature of 900°C, the oxidation weight gain increases dramatically. The TGA results indicate that the activation energy of SPHC steel is 146.19 kJ/mol at the temperature of 500°C~ 900°C, and an oxidation kinetic model was set up for variable temperature. Based on the temperature change during rolling process, numerical simulation of oxide scales evolution was carried out for SPHC steel, and the simulation result agreed well with measured ones. It can provide a basis for estimating the scale growth and controlling the temperature on site.