Effect of FeO Content in Laterite Nickel Slag on the Corrosion Behaviour of Refractory Materials

摘要

The corrosion behaviors of chrome corundum/magnesia in laterite nickel slag were investigated by static crucible method. The results show that the molten slag can penetrate into chrome corundum or magnesia which are used as lining materials in smelter furnace, and the corrosion can occur at the slag-refractory interface and the inner area of the refractories as well. Both the penetrated amount of slag and the penetration depth of Fe, Si increase with increasing FeO content (10-25 wt%) in slag. Such penetration in magnesia is stronger than that in chrome corundum under the same corrosion conditions, as more pores in magnesia may provide channels for slag penetration and corrosion product transportation. A damage of the refractory linings and short service life of smelter furnace may happen during metallurgical processing slag with high FeO content.