SCC BEHAVIOR OF ALLOY 152 WELD IN A PWR ENVIRONMENT

摘要

The objective of this work is to determine the crack growth rates (CGRs) in a simulated PWR water environment for Alloy 152. In order to meet the objective, specimens made from a laboratory-prepared Alloy 152 double-J weld in the as-welded condition were tested. For the SCC CGR measurements, the specimens were pre-cracked under cyclic loading in a primary water environment, and the cyclic CGRs were monitored to determine the transition from the fatigue transgranular fracture mode to the intergranular SCC fracture mode. The environmental enhancement of cyclic CGRs for Alloy 152 was minimal; nevertheless, the transition from transgranular to intergranular cracking was successful. Weld samples tested from the single heat of Alloy 152 exhibited SCC CGR rates of 10~(-11) m/s in the simulated PWR environment at 320°C, which was about an order of magnitude lower than typical for Alloy 182.