ELONGATIONAL RHEOLOGY AND MECHANICAL PROPERTIES OF BIODEGRADABLE PLA/PBSA BLENDS

摘要

Blends of poly(lactic acid) (PLA) and poly[(butylene succinate)-co-adipate] (PBSA) were prepared using a twin screw extruder. The morphology of the blends was examined using scanning electron microscopy (SEM). Elongational flow properties of the blends and pure components were studied. A strong strain hardening behavior was observed for PLA/PBSA blends, in which PBSA forms the continuous phase (PBSA wt% ≥ 50). The results of tensile test showed that even for blends containing only 10wt% PBSA, elongation at break increased significantly. By the addition of PBSA to PLA, a transition from brittle behavior (observed for pure PLA) to ductile behavior was observed.