Rehabilitation of Steel Bridge Girders with Corroded Ends Using Ultra-High Performance Concrete

摘要

The end corrosion in steel girders at the bearings due to joint leakage is a significant problem in many of the old bridges around the nation. This critical damage impairs the shear and bearing capacities of girders. This paper discusses a novel method for retrofitting the corroded ends of steel bridge girders using ultra-high performance concrete (UHPC) encasings. This repair method involves casting thin UHPC panels on each side of girder web. Shear studs welded to undamaged portion of the web and flange engage the UHPC panels and provide an alternate load path. This repair method is expected to be superior to the current practice of attaching steel cover plates. It can be easier to design and install, reduce obstruction to traffic during the repair, prevent future corrosion to the girder end, and reduce the total cost of repair. To investigate the effectiveness of the repair in recovering the capacity of the corrosion damaged girders, three large-scale experiments were performed on the undamaged, damaged and repaired rolled girders. It was found that a 1 /4-in. thick UHPC panel cast two-third of the height of the girder effectively restores the bearing capacity. A high fidelity finite element model was created from the results of the large-scale experiments. This model was then used to design eight repair techniques for full size plate and rolled girders with heavy corrosion damage. This innovative repair method may offer the bridge design community a superior alternative retrofit method for large scale application on our aging bridges.