Characterization of Direct and Converse Piezoelectricity of Cellulose Based Electro-Active Paper

摘要

In-plane piezoelectric charge constant of Electro-Active paper (EAPap) was investigated based on direct and converse piezoelectric effects. EAPap samples were made with cellulose film with very thin gold electrode coated on both sides of the film. To characterize direct piezoelectricity of EAPap, induced charge was measured when mechanical stress was applied to EAPap. In-plane piezoelectric charge constant was extracted from the relation between induced charge and applied in-plane normal stress. To investigate converse piezoelectricity, induced in-plane strain was measured when electric field was applied to EAPap. Piezoelectric charge constant was also extracted from the relation of induced in-plane strain and applied electric field. Piezoelectric charge constants obtained from direct and converse piezoelectricity are 31 pC/N and 178 × 10~(-12)m/V for 45 degree sample, respectively. Measured piezoelectric charge constants of EAPap provide promising potential as a piezoelectric material.