In-situ Fracture Behavior of AZ51 and AZT513 Alloy

摘要

The fracture behavior of Mg-5Al-1Zn and Mg-5Al-1Zn-3Sn alloy was investigated by direct observation of microfracture process using an in-situ loading stage installed inside a scanning electron microscope chamber. Crack was initiated at the interface of Mg/second-phase particles or second-phase particles. Fracture of the alloys was predominantly dimple or/and quasi-cleavage failure. The improvement of what could be explained by mechanisms of blocking of crack or shear band propagation, formation of multiple shear bands, crack blunting and shear band branching.