Microstructure and Wear Performance of Spray Fused NiCrBSiC/WC Composite Coatings

摘要

Characterization of flame sprayed and furnace fused NiCrBSiC alloy coatings with two different carbon contents and 15～45 wt.% WC-Co addition is described in terms of microstructure, microhardness, and differential thermal analysis. Microstructural development of these coatings before and after fusing treatment is discussed to identify the precipitates in the coatings. Optimum fusing conditions (time and temperature) for wear testing sample are investigated in terms of microhardness and porosity of the coatings. Wear performance of these coatings is also investigated by two-body and three-body abrasive and dry sliding wear experiments. Optimum tungsten carbide content of the coatings is also selected to improve wear performance and thus enhance the service life of the process roll for cold rolling steel plant. Finally, microstructure and microhardness of the furnace and induction fused coatings are compared with emphasis on the interface between the coating and the steel substrate.