Lepidocrocite to Maghemite to Hematite: A way to have Magnetic and Hematitic Martian Soil

摘要

We examined decomposition products of lepidocrocite, which were produced by heating the phase in air at temperatures up to 525 C for 3 and 300 hr, by XRD, TEM, magnetic methods, and reflectance spectroscopy (visible and near-IR). Single-crystal lepidocrocite particles dehydroxilated to polycrystalline particles of disordered maghemite which subsequently transformed to polycrystalline particles of hematite. Essentially pure maghemite was obtained at 265 and 223 C for the 3 and 300 hr heating experiments, respectively. Its saturation magnetization (J(sub s)) and mass specific susceptibility are approximately 50 A(sq m)/kg and approximately 40 cubic micrometers/kg, respectively. Because hematite is spectrally dominant, spectrally-hematitic samples (i.e., characterized bv a minimum near 860 nm and a maximum near 750 nm) could also be strongly magnetic (J(sub s) up to approximately 30 A(sq m)/kg) from the masked maghemite component. TEM analyses showed that individual particles are polycrystalline with respect to both maghemite and hematite. The spectrally-hematitic and magnetic MhHm particles can satisfy the spectral and magnetic constraints for Martian surface materials over a wide range of values of Mh/(MhHm) and as either pure oxide powders or (within limits) as components of multiphase particles. These experiments are consistent with lepidocrocite as the precursor of MhHm assemblages on Mars, but other phases (e.g., magnetite) that decompose to Mh and Hm are also possible precursors. Simulations done with a copy of the Mars Pathfinder Magnet Array showed that spectrally hematitic MhHm powders having J(sub s) equal to 20.6 A(sq m)/kg adhered to all five magnets.