Effect of calcium chloride on physical properties of calcium-enriched mixture cement

摘要

The aim of this study was to evaluate the effect of adding 10% calcium chloride (CaCl2) on the setting time, solubility and the pH of calcium-enriched mixture (CEM) cement. Setting time was assessed in accordance with American Dental Association specification N degrees 57. Solubility was measured at 24 and 72h, 7 and 14 days in hydrated and dehydrated conditions by calculating weight change. The pH of MiliQ water in which the CEM cement samples were immersed was measured immediately after each time interval with and without the addition of CaCl2. The data were analysed using the Mann-Whitney U-test and the Student's t-test. The initial setting time was significantly decreased after the addition of 10% CaCl2. The pH of water increased immediately when in contact with the cements in both groups. The weight loss of hydrated and dehydrated specimens was more than 3% and was significantly reduced by the addition of 10% CaCl2.