Facile preparation of transparent and conductive polymer films based on silver nanowire/polycarbonate nanocomposites

摘要

Silver nanowires (AgNW) synthesized by a solvothermal method were incorporated into a polycarbonate matrix by a solution mixing procedure. Films with a thickness around 18 μm were obtained, showing a good distribution of the wires within the polymer matrix. The thermal stability of the polymer matrix increased significantly, with the main decomposition peak shifting up to 74 ° C for an AgNW loading of 4.35 wt%. The percolation threshold was obtained at very low AgNW content (0.04 wt%), and the composite electrical conductivity at the maximum loading (4.35 wt%) was 41.3 Ω cm. Excellent transparency was obtained at the percolation threshold, with negligible reduction in the transmittance of the polymer matrix (from 88.2 to 87.6% at 0.04 wt% loading of AgNW). In addition, the polymer matrix protected the silver nanowires from oxidation, as demonstrated by the XPS analysis.