马口铁

摘要： 罐头是日常生活中比较常见的食物,也是重要的救灾物资。根据罐头的包装材质不同,市售罐头可粗略分为马口铁听装和玻璃瓶装两种,还有极少数不常见的软包装罐头。罐头容易储存,但变质却不容易被发现。甄别罐头质量,要一看、二听、三尝。其中,一看和二听,主要是开罐之前的甄别手法,开罐之后就需要亲自尝一尝了。

摘要： 不停地开枪射击之后,维克斯机枪里的水会沸腾,这时,士兵们可以拆开枪管倒出热水泡茶喝。这是从一战纪录片里学到的冷知识。那杯让士兵暂时忘掉炮火的茶,弥散着袅袅热气,看上去很好喝。只是看上去。蒂莫西,小说《战地厨师》中的主人公、美军G连管理部炊事兵,说战场上,不仅茶,连用马口铁小锅煮出的咖啡,味道都“像淡泥水”。

摘要： 通过采用正交组合优化设计的方法对0.2 mm厚的马口铁薄壁激光对焊工艺进行优化,利用显微硬度计、光学显微镜等工具,研究激光功率、脉冲宽度、脉冲频率以及焊接速度对焊接接头显微组织及力学性能影响的规律,并与厂家生产的马口铁罐身的激光焊焊缝进行对比分析.研究结果表明:采用激光焊接法可实现0.2 mm马口铁薄壁高速及稳定焊接,且焊接之后的热影响区范围小;经过激光对焊后与母材对比发现,焊缝处显微组织发生明显改变,且焊缝的强度高于薄壁侧母材的强度.

摘要： 以废旧马口铁为基体,Ni粉、Cr粉为覆膜材料,通过活化反应烧结法制备了Ni-Cr-Fe三元薄膜合金电极.采用X射线衍射分析(XRD)、场发射扫描电镜(SEM)、X射线能谱分析(EDS)、X射线光电子能谱分析(XPS)等对电极的物相、形貌结构、元素分布进行表征,并研究了电极材料的析氢机理,通过循环伏安曲线(CV)、线性极化曲线(LSV)、电化学交流阻抗(EIS)等方法测试了电极材料的电催化析氢性能.研究结果显示,在室温条件下,Ni-Fe二元合金电极材料在6 mol/L KOH溶液中的析氢过电位为-0.59 V,交换电流密度为20.6 mA/cm2,Tafel斜率为121.3 mV/dec.同样条件下,调节Cr含量可提高析氢催化活性,Ni-30％Cr-Fe(质量分数,下同)三元薄膜合金电极材料的析氢催化活性最强,其析氢过电位仅有-0.39 V,交换电流密度为30.9 mA/cm2,Tafel斜率为78.1 mV/dec,经28160 s开路电位测试,电极材料的开路电位(η)从-0.87 V变化为-0.69 V,仅增加18 mV,表明析氢电极的化学稳定性好.

摘要： 介绍了马口铁的用途及特性,通过对宁波钢铁马口铁基板化学成分、性能及生产工艺参数的设计,进行现场工业性生产试验,分析了影响马口铁基料性能的主要因素,并提出了化学成分、卷取温度、表面质量、尺寸精度等控制要点,产品经冷轧镀锡后,满足了终端用户对产品的质量要求.

摘要： 刀削面是山西的地方小吃,其制法较独特。家庭制作,首先要制备一把削面的刀:选择一块0.3~0.5 mm厚的不锈钢板或白铁、马口铁片,裁成18 cm长,12 cm宽的长方形。将长边的一侧卷回3 mm,另一侧磨锋做刀口,并顺刀口稍锤,使其弯曲,即成削面的刀子。如没有合适的材料制作刀,用菜刀也可以,但拿着稍重些,且削出的面平一些。

摘要： 在投产初期,镀锡基板表面存在粘钢纹、太阳线、色差、斑迹、擦伤等缺陷,同时物理性能方面存在屈服现象,导致产品质量不稳定,对马口铁的生产造成不良影响。通过对现场数据的跟踪、收集、分析、对比,同时查阅大量技术文献,并且根据现场实际运行情况,找到其原因所在,并采取了相应的改进措施,有效改善了马口铁基板的整体质量,满足了食品级马口铁质量的要求,为保证后续镀锡机组的成品品质奠定了坚实的质量基础。

摘要： 我小时候特别喜欢吃水果罐头,却总是因为打不开罐头的盖子而烦恼。我的爸爸是军人,常年驻守外地,没有了大力士的帮助,我就只能“望盖兴叹”了。妈妈为了让我吃上美味的罐头,也是五招八式全用上了,但有时候还是打不开盖子。

摘要： 由于马口铁产品轧制厚度薄,表面质量要求高,因此对冶炼和连铸的工艺要求更为严格.马口铁的表面缺陷,特别是孔洞缺陷,严重制约着当前马口铁系列产品产能的提高以及产品自身性能的提升.马口铁孔洞缺陷的最根本原因是由于钢水洁净度控制不佳,马口铁钢水洁净度控制技术成为马口铁生产过程的关键技术之一.通过扫描电镜、大样电解、光学显微镜等手段对其钢中夹杂物进行了检验分析,发现微观和大型夹杂物的主要组成均为Al-Ca-Mg复合氧化物夹杂物,同时发现含有钠、钾的来源于结晶器保护渣的大型夹杂.为减少夹杂的产生,采用了铝、镁、钙、钡复合脱氧替代单纯的铝脱氧及黏度较低的保护渣.

摘要： BOPET/马口铁复合层压材料是近年来在铁制罐包装领域特别是食品、饮料包装罐行业迅速崛起的新兴发展方向.该覆膜铁材料以其制造过程中无污染、保障被包装物在流通环节中的卫生安全、罐体在废弃后便于回收利用等方面具有相较于传统制罐使用涂料技术具有无可比拟的优势.聚对苯二甲酸乙二醇酯(PET)经过双向拉伸、热定型后表现出优异的力学及化学、物理稳定性使得其在软包装领域具有无可替代的地位,但作为与马口铁直接热封的薄膜材料使用,由于其高的结晶性导致其几乎不可能完成工艺过程.因此,如何解决其具有热封性能并不降低其其他主要性能如强度、阻隔性、成膜性等是完成BOPET/马口铁进行直接热封的关键技术问题.报道一种从合成变异结构的PET原料入手,设计出具有较低熔点、较低结晶度、较高特性粘度（有利于成膜）的PET原料,并经固相增粘后进行拉膜的试验研究,对所研制的薄膜进行了性能表征表明其完全满足热复合马口铁的应用要求,达到了预期研究目标.

摘要： 本文通过对第一炼钢厂生产马口铁采用的不同工艺的生产稳定性、产品质量及生产成本的对比分析,提出生产马口铁所需采用的生产工艺路线和前提条件.在基本满足下游用户产品质量的基础上,通过对马口铁单、双联工艺优化对比,找出最佳工艺路线,保证我公司新品种开发的成本优势。

摘要： 本文简要分析了在包装领域应用非常广泛的马口铁的结构和特点，详细探讨了马口铁在印刷过程中马口铁表面性能、底漆涂料、油墨、涂布光油性能、烘干温度和不同印刷工艺对印刷牢度的影响和控制要点，这对马口铁印刷质量的提高有一定的指导作用。

摘要： 金属包装得益于钢铁行业的技术进步和回收利用，对环境的影响已大为减少，也节约了资源，同时比较了不同食品加工和包装方式的生态效应，也表明罐头食品的生态效应，是环境和成本利益相结合的最好表现。

摘要： 本文简要介绍了高保真印刷技术的原理,阐述了高保真印刷在印刷行业的发展,重点说明了高保真印刷技术在印铁行业尤其是宝印公司的应用,以及该技术对印铁行业的发展促进作用进行了展望.

摘要： Surface morphology of alloy layer of tinplate was studied by scanning electron microscope (SEM) .It was found that the cavity of alloy layer was a critical factor causing rapid decline of the corrosion resistance of tinplate. Rely on the layer on layer debonding technology of glow discharge spectrum (GDS) ,the content of C and 0 on the boundary of alloy layer and black plate was analyzed.lt proved for the first time, making use of experimental simulation, that the formation of cavity of alloy layer was due to incorrect pretreatment of black plate before electrotinning. By electrochemical atomic force microscope ( E-CAFM) , the corrosion characteristic of cavities of alloy layer of tinplate was studied on line and in situ, which proved that the cavity of alloy layer was the internal factor causing perforating corrosion of tinplate when applied to food packaging material. Through measuring the corrosion depth of cavity of alloy layer in situ after different corrosion time, it was found that the dynamic equation of pitting corrosion generated in the cavity of alloy layer conformed to logarithm law.

摘要： Surface morphology of alloy layer of tinplate was studied by scanning electron microscope (SEM) .It was found that the cavity of alloy layer was a critical factor causing rapid decline of the corrosion resistance of tinplate. Rely on the layer on layer debonding technology of glow discharge spectrum (GDS) ,the content of C and 0 on the boundary of alloy layer and black plate was analyzed.lt proved for the first time, making use of experimental simulation, that the formation of cavity of alloy layer was due to incorrect pretreatment of black plate before electrotinning. By electrochemical atomic force microscope ( E-CAFM) , the corrosion characteristic of cavities of alloy layer of tinplate was studied on line and in situ, which proved that the cavity of alloy layer was the internal factor causing perforating corrosion of tinplate when applied to food packaging material. Through measuring the corrosion depth of cavity of alloy layer in situ after different corrosion time, it was found that the dynamic equation of pitting corrosion generated in the cavity of alloy layer conformed to logarithm law.

摘要： Surface morphology of alloy layer of tinplate was studied by scanning electron microscope (SEM) .It was found that the cavity of alloy layer was a critical factor causing rapid decline of the corrosion resistance of tinplate. Rely on the layer on layer debonding technology of glow discharge spectrum (GDS) ,the content of C and 0 on the boundary of alloy layer and black plate was analyzed.lt proved for the first time, making use of experimental simulation, that the formation of cavity of alloy layer was due to incorrect pretreatment of black plate before electrotinning. By electrochemical atomic force microscope ( E-CAFM) , the corrosion characteristic of cavities of alloy layer of tinplate was studied on line and in situ, which proved that the cavity of alloy layer was the internal factor causing perforating corrosion of tinplate when applied to food packaging material. Through measuring the corrosion depth of cavity of alloy layer in situ after different corrosion time, it was found that the dynamic equation of pitting corrosion generated in the cavity of alloy layer conformed to logarithm law.

摘要： 本发明特别涉及一种镀层马口铁的制备方法及镀层马口铁，属于金属材料处理技术领域。一种镀层马口铁的制备方法，包括如下步骤：得到钢板基板；将钢板基板经碱洗和酸洗，得到预处理基板；于预处理基板表面电镀镍，得到第一镀层基板；于第一镀层基板表面电镀锡，得到第二镀层基板；将第二镀层基板经软熔和钝化，得到镀层马口铁。其通过在钢板基板表面闪镀一层镍，抑制镀锡板表面锡铁之间合金化程度，提高了锡层在镀锡板表面的均匀性及表面自由锡含量，解决了低锡量镀锡板完全合金化耐蚀性差的问题。

摘要： 本发明属于盒罐技术领域，尤其涉及一种马口铁罐、马口铁封口结构及其加工工艺。马口铁封口结构包括罐身和罐底，罐身的底缘设有罐身弯折件，罐身弯折件包括依序连接的第一上横折部、第一竖折部和第一下横折部并形成第有一U型口；罐底的周缘设有罐底弯折件，罐底弯折件包括依序连接的第二下横折部、第二竖折部和第二上横折部并形成有第二U型口；第一U型口与第二U型口的开口朝向相反，第二上横折部扣入第一U型口内并被第一上横折部和第一下横折部压紧，第一下横折部扣入第二U型口内并被第二上横折部和第二下横折部压紧。利用相互压紧连接的罐身弯折件和罐底弯折件形成的几道折弯结构，形成的封口的密封性更强，防漏水气效果更佳。

摘要： 本申请涉及复合镀层的马口铁生产工艺及马口铁，包括S10，前处理：对钢基体进行脱脂和酸洗；S20，电镀锡：在钢基体上电镀锡，然后漂洗，以在钢基体的表面形成纯锡层；S30，电镀铬：在已完成步骤S20的钢基体表面电镀铬并进行漂洗，以在纯锡层的表面形成铬金属层和铬水合氧化物层；S40，涂油：在已完成步骤S30的钢基体表面涂油，以形成油膜层。所述马口铁生产工艺，以及应用该工艺形成的马口铁具有镀锡镀铬复合镀层，基于金属铬的防腐蚀性能优良，外表面的镀铬层主要是起到防腐蚀的作用，同时内层的锡具有良好的焊接性能，在需要焊接时起到助焊剂的作用，保证制罐时的焊接质量，使镀铬铁也能够制作三片罐，且降低了成本。

摘要： 本发明公开了一种用于检测马口铁金属罐盖的传送方法，包括底座和中心柱，所述中心柱固定连接在底座顶端的中间位置处，所述中心柱的外部活动连接有套筒。该用于检测马口铁金属罐盖的传送方法通过竖板的一侧之间活动连接有转轴，在使用时，启动驱动电机，驱动电机驱动小齿轮转动，小齿轮通过齿圈驱动套筒在中心柱的外部转动，从而带动传送盘转动对罐盖进行传送，与此同时启动下料电机，下料电机驱动转轴转动，转轴带动拨片转动，当罐盖在传送盘上检测之后传送至最前端时会被拨片自动拨下，这样就实现了自动下料，无需人工，节约劳动力，解决的是不方便进行自动下料，占用劳动力的问题。

摘要： 本发明公开了一种控制马口铁起筋高度的方法，属于冷轧技术领域。该方法包括依次进行的炼钢、热轧、酸连轧、连续退火和电镀锡工序，其中，在热轧工序中控制板凸度为25~30μm，在酸连轧工序中控制相对长度差＞8 I‑uint。本发明能够将其起筋高度控制在0.15mm以内，提高产品合格率。

摘要： 本实用新型属于盒罐技术领域，尤其涉及一种马口铁罐及马口铁封口结构。马口铁封口结构包括罐身和罐底，罐身的底缘设有罐身弯折件，罐身弯折件包括依序连接的第一上横折部、第一竖折部和第一下横折部并形成第有一U型口；罐底的周缘设有罐底弯折件，罐底弯折件包括依序连接的第二下横折部、第二竖折部和第二上横折部并形成有第二U型口；第一U型口与第二U型口的开口朝向相反，第二上横折部扣入第一U型口内并被第一上横折部和第一下横折部压紧，第一下横折部扣入第二U型口内并被第二上横折部和第二下横折部压紧。利用相互压紧连接的罐身弯折件和罐底弯折件形成的几道折弯结构，形成的封口的密封性更强，防漏水气效果更佳。

摘要： 本实用新型属于马口铁罐杀菌领域，具体的说是一种马口铁罐杀菌装置，包括杀菌室，所述杀菌室内设置有输送机，所述输送机外在杀菌室两端设置有防尘罩，所述杀菌室内在输送机正上方设置有喷淋装置，所述杀菌室在喷淋装置一侧设置有烘干室。该马口铁罐杀菌装置，通过在输送机外侧设置有杀菌室，杀菌室内设置有喷淋装置和烘干室，喷淋装置先对输送过程中的马口铁罐进行喷淋除菌，同时回收水箱可对喷淋水进行回收至水箱内，从而再次使用节能环保，烘干室内设置有高温消毒管和风机对马口铁罐进行高温烘干消毒，第二电动伸缩杆和夹紧气缸可对马口铁罐进行夹紧上升调节位置，从而便于提高烘干效率，有利于提高杀菌效果。

摘要： 本实用新型提供了一种异型马口铁盖集盖装置，解决了目前集盖机构存在落盖难以及落盖不稳定的问题。其特征在于：所述落盖孔左右的两侧设有分盖磁铁，所述落盖孔的前后端均设有安装座，所述安装座安装有弹性卡块，所述弹性卡块之间距离小于落盖孔直径。分盖磁铁将罐盖各自分开使罐盖不叠加，部分位于落盖孔内的弹性卡块用于支撑罐盖，防止罐盖掉落，吸盖机构吸取罐盖时，弹性卡块可允许罐盖通过，同时阻挡下一个罐盖，还不会对罐盖造成损坏，可以保证稳定落盖，同时整体结构简单、成本低。

摘要： 本实用新型提供一种马口铁罐生产用扣骨机的接料装置，包括工作台和安装在工作台上用于生产马口铁罐的扣骨机，所述扣骨机包括有扣骨模具，所述扣骨模具的出料端焊接有两根导料杆，所述工作台上放置有接料盘，所述马口铁罐经导料杆导出竖直的落在接料盘内放置，所述工作台上安装有可推动接料盘往复式纵向移动和横向移动进行均匀接料的移动装置，所述工作台上固定连接有安装板，所述安装板的侧壁安装有拨动马口铁罐顺着导料杆滑出的拨料机构。该装置能够自动的将扣骨后的马口铁罐导出，罐口朝上均匀的摆放在接料盘内。

摘要： 本实用新型提供了一种便于密封的压扣式马口铁罐,涉及马口铁罐领域，包括马口铁罐、铁罐盖、压扣组件和密封组件，所述铁罐盖盖设在马口铁罐的上方，所述压扣组件设有两组，两组所述压扣组件分别位于铁罐盖的两侧，所述马口铁罐的内部设有密封组件，所述压扣组件包括轴承座、撬杆、固定块和弹簧，所述轴承座上铰接有撬杆，所述撬杆的一端铰接有固定块，所述固定块与撬杆之间连接有弹簧；本实用新型通过将固定块转动至与撬杆齐平的位置，弹簧伸长，下压固定块，撬杆的另一端将铁罐盖起出，省时省力，便于操作。