摘要： 为了研究复合纳米TiO2材料的磁电阻特性,通过磁控溅射方法和原位退火工艺制备了Co掺杂TiO2薄膜样品。利用X射线衍射仪和扫描探针显微镜观测薄膜样品的微结构特征，利用振动样品磁强计和多功能物理性质测量系统测试样品的磁特性和磁电阻。结果表明，Co掺杂量对TiO2薄膜的磁电阻特性有重要影响：磁性金属含量较高的薄膜样品出现较大的磁电阻，磁电阻峰值为－14%，峰值温度为250K；磁性金属含量较低薄膜样品具有较小的磁电阻值；由于Co掺杂影响了薄膜的微结构和导电性，导致出现了特殊的磁电阻效应。%In order to study the magnetoresistance of TiO2 nanofilms, the Co-doped TiO2 nanofilms have been fabricated by dc facing-target magnetron sputtering and subsequently annealed in situ vacuum. The phase identification of samples has been carried out by X-ray diffraction. The morphologies and domain structures were observed by scanning probe microscope. Magnetic properties were measured by vibrating sample magnetometer. The magnetoresistance were measured by physical property measurement system. The result shows that the magnetoresistance of the films depends strongly on the Co concentration.The magnetoresistance of film is tested under different temperatures,when the temperature is 250K that there exist peak values at -14%. The Co doping affectes the structure and conductivity,eventually leads to the special phenomenon of the magnetoresistance.

摘要： 以四氯化钛为初始反应物,采用水解沉淀法合成纳米TiO2薄膜.结合XRD、TEM以及FTIR等手段对TiO2/硅藻土基多孔陶瓷复合材料的晶体结构和形貌进行了表征;以复合材料为空气净化器芯体,甲醛为降解对象,对光催化降解动力学进行了探讨.结果表明:纳米TiO2经600°C煅烧后为锐钛矿型,平均粒径约10.6 nm,纳米TiO2薄膜牢固包覆于载体表面(膜厚300～450 nm).包覆层与TiO2薄膜之间的界面上形成了Si-O-Ti键.甲醛初始浓度为1.302 mg/m3,紫外光照240 min,甲醛去除率达到94.6％.动力学研究表明:可用Lang-muir-Hinshelwood动力学方程来描述甲醛光催化降解反应,该气相光催化一级反应时的反应速度常数为0.576 mg/(m3·min),吸附系数为0.048 m3/mg.并建立了甲醛的气相光催化动力学方程.

摘要： 采用溶胶-凝胶法在氧化铟锡(ITO)导电玻璃上制备了纳米TiO2薄膜电极,研究了不同制备条件下TiO2薄膜的光电化学响应.利用X射线衍射仪对纳米TiO2的晶型结构进行了分析,利用原子力显微镜(AFM)对薄膜的表面形貌进行了表征.结果表明:随煅烧温度升高,锐钛矿(101)晶面的衍射峰强度增强;加入抑制剂且煅烧温度为650°C时制备的纳米TiO2为锐钛矿晶型,薄膜粒度分布均匀、尺度适宜,且表面存在一定孔隙.暂态电流测试表明:在光强为6.6mW/cm2、极化电位为+0.3V时,随着预吸附时间的延长,瞬时产生的峰值电流逐渐增大;当预吸附时间为300s时,随着煅烧温度的升高,TiO2薄膜电极对H2O分子的催化氧化光电流由24.2μA(450°C)提高到49.0μA(650°C).

摘要： TiO2 nanofilms on surface of fused silica were fabricated by Ti ion implantation and subsequent thermal annealing in oxygen ambience. The silica glasses were implanted by 20 k V Ti ions to 1.5 × 1017ions/cm2 on an implanter of metal vapor vacuum arc(MEVVA) ion source. Effects of annealing parameters on formation,growth and phase transformation of the TiO2 nanofilms were studied in detail. Optical absorption spectroscopy,Raman scattering spectroscopy, X-ray photoelectron spectroscopy, scanning electron microscopy and transmission electron microscopy measurements were done to figure out formation mechanism of the TiO2 nanofilms.The formation of TiO2 nanofilms was due to out-diffusion of the implanted Ti ions to the substrate surface,where they were oxidized into TiO2 nanoparticles. Formation, phase, and thickness of the TiO2 nanofilms can be well tailored by controlling annealing parameters.

摘要： 以钛酸丁酯为原料,采用改进的溶胶-凝胶法制备ITO负载纳米TiO2薄膜,通过XRD、SEM和UV-Vis等检测方法对薄膜样品进行表征,并考察其在双室光电化学池中制氢反应的光催化活性.结果表明:纳米TiO2薄膜为锐钛矿-金红石混晶结构,当溶胶中P25粉末含量为0.09g/mL时制备的TiO2薄膜产氢量最大,光催化性能较好.

摘要： As an environmentally friendly pollution management technology , TiO2 photo catalytic technique has caused attention for applica-tion as catalysis in the disinfecting of drinking water , which has advantages of non -toxic, high catalytic activity , stable chemical proper-ties and so on.Based on the mechanism of TiO2 photo catalysis, the experiment of the main influencing factors on TiO 2 photo catalytic oxi-dation performance and launched the sterilization experiment with TiO 2 has studied.The paper presents the feasibility of TiO 2 photo-cata-lytic application in drinking water disinfection and puts forward relevant suggestions and measures .%TiO2光催化氧化技术作为一种环境友好型的污染治理技术，具有无毒、催化活性高、化学性能稳定等优点，将其应用于饮用水消毒的研究受到重视。笔者通过介绍TiO2光催化的作用机理，研究影响TiO2光催化氧化性能的主要因素及利用TiO2进行灭菌实验，阐述TiO2光催化在饮用水消毒中应用的可行性并提出相关建议和措施。

摘要： 本文以钛酸正丁酯为前驱物、乙醇作为分散剂、二乙醇胺作为螯合剂、聚乙二醇作为表面活性剂,采用溶胶-凝胶法制备得到一种TiO2溶胶,并通过乙酸或氨水作用后制得另外两种溶胶,分别在室温于ITO导电玻璃上涂制,得到5种单一粒径范围纳米TiO2薄膜和具有两种粒径范围膜层的6种纳米TiO2薄膜；XRD和SEM等测试结果表明,纳米TiO2薄膜为锐钛矿相或锐钛矿与金红石相的混合相,其粒径分布范围在15 ～ 30nm,30～ 50 nm,40 ～ 80 nm区间.采用浸渍法将所制备的膜进行染料的敏化,得到染料敏化纳米TiO2薄膜半导体光阳极,测试结果表明,在所制备的纳米TiO2薄膜中,具有两种粒径范围膜层的纳米TiO2薄膜的光电性能相对较好.%Nano-TiO2 thin films with a kind of particle size range or two kinds of particle size range were prepared on ITO conductive glass at room temperature by sol-gel method from tetrabutyl titanate(TBT)as precursor,ethanol as solvent,diethanol amine as chela-ting agent and polyethylene glycols(PEG)as surfactant in the absence or present of acetic acid or ammonia water. XRD and SEM confirmed that the crystal phases of nano-TiO2 thin films were anatase and the mixed phases of anatase and rutile,and the particle sizes of nano-TiO2 grain were variation in 15-30 nm,30 -50 nm,and 40-80 nm. The TiO2 films prepared could be sensitized by dye to form the anodes of dye-sensitized solar cells, and the results showed that the nano-TiO2 thin films with two kinds of particle size range had better photo-electric properties.

摘要： Use Ti (SO4)2 as the raw material and anhydrous sodium carbonate (Na2CO3) as the additive, TiO2 thin films are prepared by using the method of hydrothermal synthesis on the substrate of titanium successfully.The law of concentrations effect on the growth characteristics of titanium dioxide thin film、the crystallization and phase composition has been studied systematically by using the method of X-ray diffraction (XRD) and Scanning electron microscopy (SEM), the dynamics mechanism has been analyzed;The excitation characteristics of prepared TiO2 thin films has been studied by using photoluminescence spectroscopy (PL), and the laws of effect has been theoretical explained through the micro-mechanism.%　　以Ti （SO4）2为原料，无水碳酸钠（Na2CO3）为添加剂，采用水热合成法在钛合金基底上成功制备了锐钛矿相的纳米TiO2薄膜。利用X射线衍射（XRD）、扫描电子显微镜（SEM）等测试手段系统的研究了前驱体浓度对纳米TiO2薄膜生长特性、结晶特性和相组成的影响规律；利用光致激发光谱（PL）研究了所制备TiO2薄膜的光激发特性，并通过微观机制对其影响规律进行了理论解释。

摘要： 持久性有机污染物（POPs）是对人类生存威胁最大的一类污染物之一，具有毒性、难降解、可在生物体内蓄积等特点，直接威胁人类生存繁衍和可持续发展。其中二噁英被《关于持久性有机污染物的斯德哥尔摩公约》列为第一批受控的12种POPs之一。目前，最广泛使用的二噁英末端处置方法为活性炭喷射法。然而该传统方法只实现了污染的转移，反而会加重飞灰中二噁英的处置难度。本文以1,2-二氯苯(1,2-DCBz)为二噁英rn替代物进行试验预测二噁英光催化降解规律。

摘要： 持久性有机污染物（POPs）是对人类生存威胁最大的一类污染物之一，具有毒性、难降解、可在生物体内蓄积等特点，直接威胁人类生存繁衍和可持续发展。其中二噁英被《关于持久性有机污染物的斯德哥尔摩公约》列为第一批受控的12种POPs之一。目前，最广泛使用的二噁英末端处置方法为活性炭喷射法。然而该传统方法只实现了污染的转移，反而会加重飞灰中二噁英的处置难度。本文以1,2-二氯苯(1,2-DCBz)为二噁英rn替代物进行试验预测二噁英光催化降解规律。

摘要： 持久性有机污染物（POPs）是对人类生存威胁最大的一类污染物之一，具有毒性、难降解、可在生物体内蓄积等特点，直接威胁人类生存繁衍和可持续发展。其中二噁英被《关于持久性有机污染物的斯德哥尔摩公约》列为第一批受控的12种POPs之一。目前，最广泛使用的二噁英末端处置方法为活性炭喷射法。然而该传统方法只实现了污染的转移，反而会加重飞灰中二噁英的处置难度。本文以1,2-二氯苯(1,2-DCBz)为二噁英rn替代物进行试验预测二噁英光催化降解规律。

摘要： 持久性有机污染物（POPs）是对人类生存威胁最大的一类污染物之一，具有毒性、难降解、可在生物体内蓄积等特点，直接威胁人类生存繁衍和可持续发展。其中二噁英被《关于持久性有机污染物的斯德哥尔摩公约》列为第一批受控的12种POPs之一。目前，最广泛使用的二噁英末端处置方法为活性炭喷射法。然而该传统方法只实现了污染的转移，反而会加重飞灰中二噁英的处置难度。本文以1,2-二氯苯(1,2-DCBz)为二噁英rn替代物进行试验预测二噁英光催化降解规律。

摘要： 持久性有机污染物（POPs）是对人类生存威胁最大的一类污染物之一，具有毒性、难降解、可在生物体内蓄积等特点，直接威胁人类生存繁衍和可持续发展。其中二噁英被《关于持久性有机污染物的斯德哥尔摩公约》列为第一批受控的12种POPs之一。目前，最广泛使用的二噁英末端处置方法为活性炭喷射法。然而该传统方法只实现了污染的转移，反而会加重飞灰中二噁英的处置难度。本文以1,2-二氯苯(1,2-DCBz)为二噁英rn替代物进行试验预测二噁英光催化降解规律。

摘要： 采用普通玻璃基体制备了多层纳米TiO2薄膜,经透射电镜TEM观察发现其晶格条纹清晰,为晶体结构完整的混合晶型纳米二氧化钛。紫外光下用它来处理实验室中模拟的有机印染废水亚甲基蓝溶液,其脱色率78%,重复使用三次后效果基本不变,延长光催化时间,其效率仍然可以提高,而可见光下其催化效率低下。

摘要： 采用普通玻璃基体制备了多层纳米TiO2薄膜,经透射电镜TEM观察发现其晶格条纹清晰,为晶体结构完整的混合晶型纳米二氧化钛。紫外光下用它来处理实验室中模拟的有机印染废水亚甲基蓝溶液,其脱色率78%,重复使用三次后效果基本不变,延长光催化时间,其效率仍然可以提高,而可见光下其催化效率低下。

摘要： 采用普通玻璃基体制备了多层纳米TiO2薄膜,经透射电镜TEM观察发现其晶格条纹清晰,为晶体结构完整的混合晶型纳米二氧化钛。紫外光下用它来处理实验室中模拟的有机印染废水亚甲基蓝溶液,其脱色率78%,重复使用三次后效果基本不变,延长光催化时间,其效率仍然可以提高,而可见光下其催化效率低下。

摘要： 采用普通玻璃基体制备了多层纳米TiO2薄膜,经透射电镜TEM观察发现其晶格条纹清晰,为晶体结构完整的混合晶型纳米二氧化钛。紫外光下用它来处理实验室中模拟的有机印染废水亚甲基蓝溶液,其脱色率78%,重复使用三次后效果基本不变,延长光催化时间,其效率仍然可以提高,而可见光下其催化效率低下。

摘要： 采用普通玻璃基体制备了多层纳米TiO2薄膜,经透射电镜TEM观察发现其晶格条纹清晰,为晶体结构完整的混合晶型纳米二氧化钛。紫外光下用它来处理实验室中模拟的有机印染废水亚甲基蓝溶液,其脱色率78%,重复使用三次后效果基本不变,延长光催化时间,其效率仍然可以提高,而可见光下其催化效率低下。

摘要： 本发明涉及一种Ag、N共掺杂TiO2纳米薄膜的制备方法及其纳米薄膜的应用。本发明的目的是解决现有方法存在的制备工艺复杂、重复性不好和光催化性能不高的技术问题。本发明采用的技术方案为：将玻璃片放入磁控溅射仪器中样品台上，溅射室内抽真空到至少8×10‑4Pa，然后通入氩气，使得溅射室内的反应压强上升至3.2～4.3Pa，预溅射后，使用Ag靶直流溅射，在玻璃基片上制备单层Ag薄膜，然后再通过使用TiO2靶，在氩气和氮气混合气氛下，在单层Ag薄膜上射频溅射N掺杂的TiO2薄膜，最后将溅射得到的Ag和N掺杂TiO2双层薄膜经过退火处理得到Ag、N共掺杂TiO2单层薄膜。本发明方法所制备的Ag、N共掺杂TiO2单层薄膜具有可见光催化活性，能应用于液相染料的光催化降解。

摘要： 本发明公开了一种二氧化钛纳米薄膜制备方法及二氧化钛纳米薄膜，本发明属于二氧化钛纳米薄膜加工领域。本发明的二氧化钛纳米薄膜制备方法包括如下步骤：S1、提供惰性气体；S2、对惰性气体进行耦合，同时对惰性气体点火，产生惰性气体的等离子体火炬；S3、向惰性气体的等离子体火炬的内部通入反应气体，产生含有反应气体的等离子体火炬；S4、通过含有反应气体的等离子体火炬作用样品表面。本发明的二氧化钛纳米薄膜制备方法，其制备过程简单、易行，无二次污染。

摘要： 本发明公开了一种纳米二氧化钛改性薄膜，包括多层掺杂有改性离子的二氧化钛薄膜，改性离子均掺杂在二氧化钛薄膜表面，随着二氧化钛薄膜层数的增加改性离子的掺加量呈变大趋势。所述改性离子选自过渡金属、贵金属、稀土金属或非金属。本发明还公开了其梯度掺杂改性方法，该方法操作简单、成本低、易于大规模生产，在薄膜各层中梯度分布的离子有助于光生载流子的运输与传递，能有效促进光生电子-空穴的分离，使TiO2的光吸收波长红移至可见光区，所得改性薄膜为层状结构，通过离子的梯度掺杂，有效提高了薄膜的光催化性能。

摘要： 本发明涉及一种Ag、N共掺杂TiO2纳米薄膜的制备方法及其纳米薄膜的应用。本发明的目的是解决现有方法存在的制备工艺复杂、重复性不好和光催化性能不高的技术问题。本发明采用的技术方案为：将玻璃片放入磁控溅射仪器中样品台上，溅射室内抽真空到至少8×10-4Pa，然后通入氩气，使得溅射室内的反应压强上升至3.2～4.3Pa，预溅射后，使用Ag靶直流溅射，在玻璃基片上制备单层Ag薄膜，然后再通过使用TiO2靶，在氩气和氮气混合气氛下，在单层Ag薄膜上射频溅射N掺杂的TiO2薄膜，最后将溅射得到的Ag和N掺杂TiO2双层薄膜经过退火处理得到Ag、N共掺杂TiO2单层薄膜。本发明方法所制备的Ag、N共掺杂TiO2单层薄膜具有可见光催化活性，能应用于液相染料的光催化降解。

摘要： 本发明属于光电器件技术领域，具体为二维有序TiO2纳米井薄膜的制备方法及在自供能光电器件中的应用。本发明首先制备二维有序TiO2纳米井薄膜；然后以制备的TiO2纳米井薄膜为基底，分别制备与无机物层状NiO有机半导体聚苯胺的异质结复合物，再构筑自供能型光电探测器；包括以下步骤：阳极氧化、物理剥离、加热煅烧、低温水热、原位聚合等。本发明避免了光电器件复杂昂贵的制备工艺，可实现大规模器件的快速构筑；利用p‑n结的光伏效应，在零偏压驱动下使得光生载流子在内建电势作用下快速分离，实现器件的自供能，光电流稳定且响应速度超快，并对紫外光具有良好选择性，可作为节能型高频探测器和高频光电转换器，应用在光通信、军事、医疗、光电存储等领域。

摘要： 本发明提供了一种对钛基底进行预处理，在钛基底表面预植入金红石相TiO2晶种，对钛金属基底进行预保护防止其被酸或者碱性生长液刻蚀溶解，同时为TNRA的水热生长提供晶种的方法。步骤如下：（a）钛金属基底材料表面预植入金红石相TiO2薄膜；（b）水热合成法在晶种层表面生长合成TNRA。其中在钛金属表面预植入金红石相TiO2薄膜的方法包括TiCl4溶液浸渍沉积法和高温焙烧法。在钛金属基底上预植入金红石相TiO2致密薄膜后，一方面提高了钛金属基底在水热反应过程中抗刻蚀溶解能力，另一方面为TiO2纳米柱阵列的生长提供晶种，所得的TiO2纳米柱阵列的形貌可在一定程度上由预植入的TiO2薄膜的形貌控制。

摘要： 本发明公开了一种二氧化钛纳米薄膜制备方法及二氧化钛纳米薄膜，本发明属于二氧化钛纳米薄膜加工领域。本发明的二氧化钛纳米薄膜制备方法包括如下步骤：S1、提供惰性气体；S2、对惰性气体进行耦合，同时对惰性气体点火，产生惰性气体的等离子体火炬；S3、向惰性气体的等离子体火炬的内部通入反应气体，产生含有反应气体的等离子体火炬；S4、通过含有反应气体的等离子体火炬作用样品表面。本发明的二氧化钛纳米薄膜制备方法，其制备过程简单、易行，无二次污染。

摘要： 本发明公开了一种纳米二氧化钛改性薄膜，包括多层掺杂有改性离子的二氧化钛薄膜，改性离子均掺杂在二氧化钛薄膜表面，随着二氧化钛薄膜层数的增加改性离子的掺加量呈变大趋势。所述改性离子选自过渡金属、贵金属、稀土金属或非金属。本发明还公开了其梯度掺杂改性方法，该方法操作简单、成本低、易于大规模生产，在薄膜各层中梯度分布的离子有助于光生载流子的运输与传递，能有效促进光生电子-空穴的分离，使TiO2的光吸收波长红移至可见光区，所得改性薄膜为层状结构，通过离子的梯度掺杂，有效提高了薄膜的光催化性能。

摘要： 本发明涉及新型的二氧化钛纳米片层取向薄膜及其制造方法和具备该二氧化钛纳米片层取向薄膜的物品，其中薄膜以二氧化硅和二氧化钛为主成分，其表面分散着大小为纳米级，具有层状结构的二氧化钛纳米片层，在显示高的光催化活性的同时，能够长时间维持优异的超亲水性和防雾性。

摘要： 本发明公开了一种Ag掺杂TiO2纳米薄膜，以及含有该薄膜的复合材料，是通过以下方法制备得到的：(1)将钛酸四丁酯、无水乙醇、硝酸、乙酰丙酮和去离子水混合，充分搅拌，得到TiO2溶胶；(2)向上述TiO2溶胶中加入AgNO3并持续搅拌，得Ag掺杂的TiO2溶胶；(3)采用特制的陶瓷电极材料为基底，采用浸渍提拉法制得湿膜；(4)在马弗炉中焙烧，即得陶瓷电极材料与纳米TiO2涂层组成的复合材料，陶瓷电极材料上形成的结晶相薄膜即为Ag掺杂TiO2纳米薄膜。本发明的Ag掺杂TiO2纳米薄膜，具有更好的催化活性。本发明的复合材料，对苯的降解率较仅使用陶瓷电极材料提高了26％，对苯的降解率达到80％以上。