摘要： 针对强腐蚀工况下,规整填料塔的塔内件设计和选材问题,设计制造了一种适用于规整填料塔的耐腐蚀填料支撑装置。利用有限元软件模拟了不锈钢(S31603)和PTFE两种材料的填料支撑装置的结构强度和刚度。结果表明:不锈钢材料的填料支撑装置可以满足强度和刚度要求,且经济性和加工难度都比纯四氟材料要好。在此基础上,设计制造了DN400 mm的支撑和收集再分布一体化装置,该装置在含氯工况中运行良好。

摘要： 聚四氟乙烯(PTEE)是超洁净流控元件的主要材料之一。针对聚四氟乙烯机械加工后的表面粗糙度问题,从改变进给量及车刀材料选择和切削液是否使用的角度探究机械加工PTFE表面形貌的形成机理,发现了随着车刀停留时间的增加,PTFE表面粗糙度迅速降低并最终保持在一个稳定值,而车刀材料和是否使用切削液也对PTFE机械加工后的表面形貌有非常显著的影响;通过共聚焦激光显微镜和原子力显微镜(AFM),在不同的尺度下观察了加工后PTFE的表面形貌,为从微观层面解释聚四氟乙烯机械加工后表面形貌的形成提供了直观的观测结果,从而揭示了表面形貌与车削加工参数的映射关系,并为氟塑料车削工艺的优化提供了指导性依据。

摘要： Structural and technological aspects of obtaining and processing functional composite materials based on PTFE(polytetrafluoroethylene)are considered.It is shown that,due to the features of the molecular structure of the matrix polymer,within the framework of the traditional technological paradigm,prerequisites are created for the implementation of a structural paradox,which manifests itself in a decrease in the parameters of the stress-strain and tribological characteristics of composites with an increase in the degree of filling.Within the framework of the concept of multilevel modification,methodological approaches to the implementation of the energy and technological compliance of components,which reduce the negative impact of the structural paradox,are considered.

摘要： 为使全陶瓷轴承在干摩擦工况下可靠运转,选用四氟乙烯(PTFE)材质的保持架为全陶瓷轴承提供润滑。利用Rtec销/盘摩擦磨损试验机,以PTFE盘与氮化硅(Si_(3)N_(4))销为摩擦副,研究Si_(3)N_(4)/PTFE在不同载荷和转速条件下的摩擦磨损性能,通过SEM对Si_(3)N_(4)表面的转移膜形貌进行观察,分析转移膜形成原因。结果表明:在试验参数范围内,摩擦因数随着载荷的增加先降后升,随转速的增加而增加;磨损率随着载荷的增加先升后降再升,随着转速的增加而增加;PTFE/Si_(3)N_(4)摩擦副在摩擦过程中会产生PTFE转移膜,不同载荷和转速下转移膜的表面形貌存在差异,其中丝状转移膜具有最佳的减磨润滑效果;摩擦副间摩擦热上升导致磨损形式由磨粒磨损向黏着磨损转变,其中黏着磨损对PTFE的磨损率的影响较大。PTFE在干摩擦过程中产生的转移膜能起到减磨润滑作用,因此可将PTFE作为干摩擦工况下全陶瓷轴承的润滑材料。

摘要： 直接甲醇燃料电池(DMFC)可作为一种便携式能源设备。甲醇常温下为液态,拥有容易处理,能量密度高,不会对环境造成危害等优点。甲醇作为燃料时还拥有容易储存等特点。DMFC是一种简单的系统,可以作为一种电压源为小型便携式设备和低功耗的电子元件等进行供电。但市面上常用的Pt/C催化剂价格不菲,我们利用硼氢化钠还原法和共沉淀法制备了五组不同质量比的Pt-Fe;O;/C催化剂,并对其进行了SEM及EDS表征测试,随后利用电化学工作站测试了不同质量分数的甲醇时DMFC的开路电压。

摘要： 介绍了适用于PTFE分散树脂的厢式干燥、真空干燥、带式干燥和微波干燥等干燥技术,简述PTFE分散树脂在不同干燥技术应用过程中的影响因素,为PTFE分散树脂干燥技术的应用提供参考。

摘要： 以氧化铝微粉作为填料对分散型聚四氟乙烯(PTFE)进行改性,采用糊膏冷压挤出的方式制备了不同粒径、不同填充比例的PTFE改性管材,考察了改性前后的硬度、力学性能和耐久性,并利用显微镜观察了磨损面和磨屑的微观特征。结果表明,随着填充比例增加,材料的硬度增加,产品的拉伸强度和耐久性呈现先上升后下降的趋势。综合考虑,6份10μm的填充比例下,改性材料在总体性能上达到最佳。

摘要： 对苛刻工况下衬里管道的衬里材料性能进行分析,并通过研究对比国内外标准及国外专利商的工程规定,从衬四氟衬里的成型工艺、原料的性能指标及成品的各项性能等方面对国内外衬材料及方式进行全面对比,以达到对化工装置中的衬里管道材料在高温、高压、强腐蚀等苛刻工况的正确选用和应用的目的。

摘要： 通过聚四氟乙烯(PTFE)熔融共混改性高温尼龙(PPA),研究玻纤增强改性后的复合材料。通过目测和光学显微镜研究PTFE对玻纤增强PPA的表观的影响。结果发现随着共聚物的引入,复合材料注塑后表面会形成一层薄薄的树脂层。水煮测试后,随着PTFE含量增加,PPA的吸水速率逐渐下降。通过FTIR检测,样件表面可以确认有部分的PTFE。同时,PTFE的引入使复合材料在乙二醇溶剂中的前期(48 h)稳定性略有提升,而后期(1000 h)材料保留强度要低一些。该文可对提升尼龙材料的耐醇解和耐水解提供新的解决思路。

摘要： 为提高液压缸活塞用格莱圈的可靠性,在不考虑温度影响的情况下,首先通过分析它的受力,建立动密封情况下格莱圈的力学模型;然后利用ANSYS仿真再现不同介质工作压力和不同O形圈预压缩量下O形圈的接触宽度和接触位置的变化,并使用Origin软件绘制相应曲线;再使用MATLAB软件,以不同介质压力、O形圈压缩量为自变量,O形圈与耐磨环接触面宽度发生变化的量为因变量,拟合它们之间的函数关系式;最后,将格莱圈力学模型、泄漏量模型、PTFE经验磨损公式相结合,利用拟合得到的函数,提出一种计算格莱圈使用寿命的方法.计算结果表明:使用此方法计算的格莱圈使用寿命与实际使用寿命接近.这将为液压缸活塞用密封设计提供重要参考.

摘要： 本文利用自制高速摩擦试验机对PTFE编织复合材料进行干摩擦试验，研究不同条件下(载荷、速度、湿度等)对PTFE编织复合材料摩擦磨损性能的影响;利用扫描电子显微镜(SEM)对不同条件下的磨屑形貌进行分析。研究结果表明：摩擦系数随裁荷和相对湿度的增大而减小，随摩擦速度的增大而增大;磨损量随裁荷和速度的增大而增大，随相对湿度的增大先减小后增大;载荷及速度的增加显著影响材料磨损状况。

摘要： 本文利用自制高速摩擦试验机对PTFE编织复合材料进行干摩擦试验，研究不同条件下(载荷、速度、湿度等)对PTFE编织复合材料摩擦磨损性能的影响;利用扫描电子显微镜(SEM)对不同条件下的磨屑形貌进行分析。研究结果表明：摩擦系数随裁荷和相对湿度的增大而减小，随摩擦速度的增大而增大;磨损量随裁荷和速度的增大而增大，随相对湿度的增大先减小后增大;载荷及速度的增加显著影响材料磨损状况。

摘要： 本文利用自制高速摩擦试验机对PTFE编织复合材料进行干摩擦试验，研究不同条件下(载荷、速度、湿度等)对PTFE编织复合材料摩擦磨损性能的影响;利用扫描电子显微镜(SEM)对不同条件下的磨屑形貌进行分析。研究结果表明：摩擦系数随裁荷和相对湿度的增大而减小，随摩擦速度的增大而增大;磨损量随裁荷和速度的增大而增大，随相对湿度的增大先减小后增大;载荷及速度的增加显著影响材料磨损状况。

摘要： 本文利用自制高速摩擦试验机对PTFE编织复合材料进行干摩擦试验，研究不同条件下(载荷、速度、湿度等)对PTFE编织复合材料摩擦磨损性能的影响;利用扫描电子显微镜(SEM)对不同条件下的磨屑形貌进行分析。研究结果表明：摩擦系数随裁荷和相对湿度的增大而减小，随摩擦速度的增大而增大;磨损量随裁荷和速度的增大而增大，随相对湿度的增大先减小后增大;载荷及速度的增加显著影响材料磨损状况。

摘要： The paper explicates the research course, technical methods, the difficulties in the developmentprocess and solutions of glass fiber/PTFE felt filter materials. On the one hand, New glass fiber/PTFE feltfilter materials should meet the production requirement of high function and low-cost, but on the other hand,it should meet the requirement of complex working conditions.

摘要： The paper explicates the research course, technical methods, the difficulties in the developmentprocess and solutions of glass fiber/PTFE felt filter materials. On the one hand, New glass fiber/PTFE feltfilter materials should meet the production requirement of high function and low-cost, but on the other hand,it should meet the requirement of complex working conditions.

摘要： The paper explicates the research course, technical methods, the difficulties in the developmentprocess and solutions of glass fiber/PTFE felt filter materials. On the one hand, New glass fiber/PTFE feltfilter materials should meet the production requirement of high function and low-cost, but on the other hand,it should meet the requirement of complex working conditions.

摘要： The paper explicates the research course, technical methods, the difficulties in the developmentprocess and solutions of glass fiber/PTFE felt filter materials. On the one hand, New glass fiber/PTFE feltfilter materials should meet the production requirement of high function and low-cost, but on the other hand,it should meet the requirement of complex working conditions.

摘要： PTFE是氟塑料的典型代表，其发展与应用已有近60年的历史。优良的耐热性、耐化学品性能、耐候性、优良的电性能、表面性能，使PTFE材料已在多种领域得到广泛的应用。rn 随着社会技术的不断进步和发展，PTFE的新的应用和加工方法也陆续出现，与此同时为满足各种不同加工要求和使用要求的新型的PTFE树脂也不断推出。rn PTFE的另一个特点是不易加工性。PTFE的高结品度、高分子量等因素导致了它的熔体粘度相当高，即使在380°C的高温下，它的粘度也高达1011泊，比一般热塑性树脂高7~8个数量级，所以PTFE不能采用普通热塑性塑料的加工方法如挤出成型、注射成型等方法进行加工,而是将它的树脂粉末在常温下加入一定形状的模具中在压力作用下制成预制品，然后在高于其熔点的温度下加热烧结得到具有一定强度的产品。

摘要： PTFE是氟塑料的典型代表，其发展与应用已有近60年的历史。优良的耐热性、耐化学品性能、耐候性、优良的电性能、表面性能，使PTFE材料已在多种领域得到广泛的应用。rn 随着社会技术的不断进步和发展，PTFE的新的应用和加工方法也陆续出现，与此同时为满足各种不同加工要求和使用要求的新型的PTFE树脂也不断推出。rn PTFE的另一个特点是不易加工性。PTFE的高结品度、高分子量等因素导致了它的熔体粘度相当高，即使在380°C的高温下，它的粘度也高达1011泊，比一般热塑性树脂高7~8个数量级，所以PTFE不能采用普通热塑性塑料的加工方法如挤出成型、注射成型等方法进行加工,而是将它的树脂粉末在常温下加入一定形状的模具中在压力作用下制成预制品，然后在高于其熔点的温度下加热烧结得到具有一定强度的产品。

摘要： 通过将包含聚四氟乙烯粉末和成孔剂的聚四氟乙烯混合物模制成预定形状并随后除去所述成孔剂而制成聚四氟乙烯多孔体。所述聚四氟乙烯多孔体的特征在于，所述成孔剂包含(a)选自二羧酸粉末和苯甲酸粉末的一种或多种粉末和(b)有机溶剂。

摘要： 本发明公开一种疏水疏油PTFE膜的制备方法，涉及高分子材料技术领域，本发明包括以下步骤：(1)制备硅烷类防水拒油剂；(2)混料；(3)挤出；(4)压延；(5)双向拉伸；(6)热定型。本发明的有益效果在于：本发明制得的疏水疏油PTFE膜具有良好的抵抗低表面张力液体的作用，从而保障了高粉尘工况下PTFE覆膜滤料长期运行，阻力也不会发生明显上升的情况。

摘要： 通过将包含聚四氟乙烯粉末和成孔剂的聚四氟乙烯混合物模制成预定形状并随后除去所述成孔剂而制成聚四氟乙烯多孔体。所述聚四氟乙烯多孔体的特征在于，所述成孔剂包含(a)选自二羧酸粉末和苯甲酸粉末的一种或多种粉末和(b)有机溶剂。

摘要： 本申请涉及一种PTFE改性板材以及含有PTFE改性板材的PTFE耐磨滑板，属于聚四氟乙烯的技术领域。一种PTFE耐磨滑板，包括PTFE改性板材、金属板材以及环氧胶水，PTFE改性板材的制备方法为：S1、称取配料：聚四氟乙烯、玻璃纤维、碳纤维；S2、挤出成板；S3、表面改性：采用硅烷偶联剂浸泡板材，再将板材等离子体处理，并采用环氧丁烯、4‑乙烯基苯并环丁烯、4‑(2‑环氧乙烷基)乙烯基苯并环丁烯进行表面接枝改性。本申请的PTFE改性板材具有良好的导热性能与强度性能，且与环氧胶水有良好的粘结性能，使制得的PTFE滑板呈现出良好的硬度性能、耐磨性能与剥离强度。

摘要： 一种获得低分子量聚四氟乙烯(PTFE)的方法，其包括以下步骤：提供高分子量PTFE；将所述高分子量PTFE设置在由阻气屏障界定并且包含具有0.005体积％至0.5体积％的氧气量的受控气氛的腔室中；将包含所述高分子量PTFE的所述腔室气密性封闭；在所述气密性封闭的腔室中照射所述PTFE以获得所述低分子量PTFE。

摘要： 本申请提供了PTFE膜的制备方法、PTFE膜、质子交换膜、燃料电池，PTFE膜的制备方法包括如下步骤：提供PTFE乳液，向其中加入低结晶度高分子得到混合液；将所述混合液混合均匀；去除所述混合液的溶剂使所述混合液形成PTFE膜。本申请实施例提供的PTFE膜的制备方法，通过将PTFE乳液与低结晶度高分子共混后制备PTFE膜，由于PTFE的结晶度非常高，PTFE的晶区与低结晶度高分子的晶区之间容易出现缺陷，导致应力集中进而导致形成孔隙，质子能够轻易穿过这些孔隙，使得PTFE膜的传导能力增强。

摘要： 本发明公开了一种PTFE坯膜回收再利用的方法及其应用，具体涉及高分子材料技术领域。方法包括以下步骤：(1)PTFE坯膜回收初处理；(2)将膜废料加热，然后迅速冷却；(3)将步骤(2)得到的膜废料进行研磨，得到PTFE粉状浆料；再进行过滤、干燥、筛分，得到PTFE回收树脂；(4)PTFE回收树脂与航空煤油通过V型混料机进行混合，预压及压延环节得到坯膜；(5)脱脂/纵拉：将坯膜进行除油与纵向拉伸，得到胶条初体，分切得到PTFE胶条；(6)覆胶条：将PTFE胶条通过覆胶机，覆着在PTFE基材滤布上。有益效果：通过此方法对回收PTFE废旧坯膜进行破碎(液氮+机械研磨)，节约能耗，且破碎后的PTFE坯膜粉碎料能够通过一定工艺制备成PTFE胶条产品，附加值高。

摘要： 本发明公开一种耐高温、高粘性PTFE胶条的制备方法，涉及PEFE胶条技术领域，本发明包括以下步骤：(1)称取双酚F环氧树脂和戊二酸，其中羧基与环氧基团的摩尔比为1:1；(2)将羧酸化木质素与溶剂混合，溶解后，加入双酚F环氧树脂，真空抽气至脱除溶剂，得到改性后的环氧树脂；(3)将改性后的环氧树脂倒入熔化的戊二酸中得到树脂浆液，然后将浆液倒入PTFE薄膜上，固化后，得到PTFE胶条。本发明的有益效果在于：本发明制得的PTFE胶条能够耐受180°C以上温度，环氧树脂改性材料中发生酯交换反应，自我修复弥补粘合性能，收缩程度低、胶条剥离强度高，能够满足滤料对聚四氟乙烯基膜耐高温不脱落的要求。

摘要： 本发明公开了一种PTFE微滤膜及PTFE微滤膜亲水改性方法，包括以下步骤：（1）将洁净的PTFE微滤膜浸渍在无水乙醇预湿；（2）将步骤（1）处理后的PTFE微滤膜浸渍在PVA/CA混合液中至少30 min、取出，烘干表面水分；（3）将步骤（2）处理后的PTFE微滤膜放入烘箱中进行交联反应，得到改性亲水化改性的PTFE微滤膜。本发明所提供的对PTFE微滤膜亲水改性方法，通过将合适浓度的PVA与CA充分的浸入到PTFE微滤膜的微孔中，之后PVA与CA的交联反应生成高透水性的亲水性交联三维网状膜，在保证PTFE微滤透水的前提下不仅改善PTFE微滤膜的亲水性，还能提高PTFE微滤膜的的分离效能。

摘要： 本实用新型涉及PTFE膜技术领域，尤其涉及一种可提高PTFE膜耐洗涤性的PTFE膜结构，包括膜体和无纺布层，膜体设在无纺布层顶端，膜体与膜体的拼接处设有加固机构，膜体与无纺布层之间设有中间编织机构，无纺布层上开设有透气孔，无纺布层顶端位于透气孔处设有支撑机构，本实用新型通过在膜体与膜体的拼接处设置加固机构，中间分隔片固定在两个膜体之间，上连接片两侧设置第一编织环牢固编织在膜体上，可将两个膜体稳定的拼接在一起，并在中间分隔片底部设置第二编织环编织在无纺布层上，可将膜体的拼接处牢固的与无纺布层复合在一起，使膜体的拼接处不易发生断裂和翘边，提高PTFE膜的耐洗涤性能。