Manufacturing method of eco-friendly glass using coal preparation
Manufacturing method of eco-friendly glass using coal preparation
展开▼
机译:使用煤制备的环保玻璃制造方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
The present invention is a step of preparing a glass raw material by mixing 50 to 90% by weight of pumice stone, sodium carbonate (Na 2 CO 3 ) 3 to 30% by weight, and calcium carbonate (CaCO 3 ) 3 to 30% by weight generated in the process of coal selection And, melting the glass raw material at a temperature of 1150 ~ 1600 ℃, maintaining the molten result at a temperature of 550 ~ 700 ℃ for stress relief, and slowly cooling the resultant maintained at a temperature of 550 ~ 700 ℃ It relates to a method for manufacturing glass from recycled pumice stone, characterized in that it comprises the step of obtaining glass. According to the present invention, it is possible to manufacture glass at low process cost by recycling pumice stone, which is a waste generated in the process of coal selection.
展开▼
机译:本发明是通过将50至90重量%的浮石石,碳酸钠(Na 2℃> Co 3 sub>)3至30%来制备玻璃原料的步骤重量,碳酸钙(Caco 3)3至30重量%在煤选择过程中产生,并在1150〜1600℃的温度下熔化玻璃原料,保持熔融效果在550〜700℃的温度下,应力缓解,并且缓慢冷却所得的温度为550〜700℃,它涉及一种从再生浮石石材制造玻璃的方法,其特征在于它包括获得玻璃的步骤。根据本发明,可以通过再循环浮石的低工艺成本制造玻璃,这是在煤选择过程中产生的废物。
展开▼