A method for producing LiNbO3 single crystal is composed of (I) drying Li1+xNb1+xO3 (0.1=X = 0.2) base material at 150-200C, (2) mixing and crushing, (3)recrushing for 12hrs at 7200 after synthesizing, (4)heat treating at 1300C in crystal growing furnace with Mo single crystal plate seed, (5)poling at 240C which is higher than curie temp. The driving force in process (4), is capillary force and the thickness of the single crystal can be controlled by controlling that of Mo plate. This method has the advantage of low price for single crystal production and low loss of ingot during cutting.
展开▼
机译:一种LiNbO3单晶的制造方法,包括:(I)在150-200℃下干燥Li1 + xNb1 + xO3(0.1 <= X <= 0.2)基材,(2)混合并粉碎,(3)在7200下粉碎12小时。合成后,(4)用Mo单晶板晶种在晶体生长炉中在1300℃下热处理,(5)在高于居里温度的240℃下极化。过程(4)中的驱动力是毛细作用力,并且可以通过控制Mo板的厚度来控制单晶的厚度。这种方法的优点是单晶生产的价格低,切割时锭的损失小。
展开▼