A procedure to produce Construction Components Molded from usual Dimensions, 20x20x40, 20x20x20 10x20x40 ',' u 'and' 20x20x20 manufactured Machine Block,Where there is a Frague Under Black Plastic Tent, on Trestles, at a temperature of 60 * 60 * c to C, the resulting component with a Heat coefficient K between 1.20 and 1.70.Cal / m2 H * (for variant (vicemen) chip Cement Compression Strength between 4 and 8 kg / cm2 and component Weight of between 4 and 5.6 kg, Fire Retardant behavior between 350 and 450 C * C * with water Absorption and water without deformation by humidity between 50% and 65%.The Cement composition chip 1:16: 12 in the first mineralization and 1: 8 to 1: 5 in Molding such as dosage of this second stage.
展开▼
机译：生产用通常尺寸模制的建筑构件的程序，制造尺寸为20x20x40、20x20x20 10x20x40'，'u'和'20x20x20的机器块，在支架上的黑色塑料帐篷下有防冻装置，温度为60 * 60 * c C，得到的组件的热系数K在1.20和1.70之间.Cal // m2 H *（用于变体（副手）碎屑水泥抗压强度在4和8 kg / cm2之间，组件的重量在4和5.6 kg之间，耐火在350至450 C * C *之间的耐水性能，在50％至65％的湿度下吸收和保持水分不变。水泥组合物在第一次矿化中的比例为1:16:12，在成型时为1：8至1：5作为第二阶段的剂量。