Constituent for fire-resistant resin foaming body, production manner null of fire-resistant resin foaming body and fire-resistant resin foaming
Constituent for fire-resistant resin foaming body, production manner null of fire-resistant resin foaming body and fire-resistant resin foaming
展开▼
机译:耐火树脂发泡体的成分,耐火树脂发泡体的生产方式及耐火树脂发泡
展开▼
页面导航
摘要
著录项
相似文献
摘要
PURPOSE:To obtain the title composition useful for building materials, having low smoking, hardly evolving harmful substances to cause an environmental pollution in combustion, having excellent heat insulating properties and soundproofing properties, comprising a specific flame-retardant and a specific low-density PE-based resin in a specific ratio. CONSTITUTION:The objective composition comprising (A) a halogenated phosphorus-containing compound-based flame-retardant containing 50-85wt.% phosphorus and halogen, having 150-250 deg.C melting point and 0.2-50mum particle diameter and (B) a low-density PE resin having 0.910-0.930g/cm3 density and 0.5-50g/10 minutes melt flow rate in a weight ratio of the component A/B of 0.05-0.45. The composition is molded, heated and crosslinked and foamed to give flame-retardant resin foamed body.
展开▼
机译:目的:获得一种用于建筑材料的标题组合物,该组合物具有低烟度,几乎不释放有害物质而在燃烧中造成环境污染,具有优异的隔热性能和隔音性能,并包含特定的阻燃剂和特定的低密度PE基树脂的特定比例。组成:一种目标组合物,其包含(A)卤化的含磷化合物基阻燃剂,该阻燃剂包含50-85wt。%的磷和卤素,熔点为150-250℃,粒径为0.2-50μm,并且在组分A / B的重量比为0.05-0.45的情况下,具有0.910-0.930g / cm 3密度和0.5-50g / 10分钟熔体流动速率的低密度PE树脂。将该组合物模塑,加热和交联并发泡以得到阻燃树脂发泡体。
展开▼