STOCK FOR STEEL SHEET FOR CAN, EXCELLENT IN RIDGING RESISTANCE AND DEEP DRAWABILITY AFTER COLD ROLLING-ANNEALING
STOCK FOR STEEL SHEET FOR CAN, EXCELLENT IN RIDGING RESISTANCE AND DEEP DRAWABILITY AFTER COLD ROLLING-ANNEALING
展开▼
机译:罐头用钢板料,在冷轧退火后具有出色的耐拉拔性和深延展性
展开▼
页面导航
摘要
著录项
相似文献
摘要
PROBLEM TO BE SOLVED: To enable the production of a cold rolled steel sheet for can, having ridging resistance and deep drawability, by specifying the average crystalline grain size of a steel sheet containing specific essential components and also specifying the colony size and the degree of orientational concentration in the colony, respectively. ;SOLUTION: A steel, which has a composition containing, as essential components, 0.0005-0.0150%, by weight, C, ≤0.10% Si, 0.1-0.6% Mn, ≤0.02% each of P and S, 0.015-0.15% Al, and ≤0.02% N and having the balance Fe with inevitable impurities, is used. Moreover, the average crystalline grain size (d) and the average colony size are regulated to ≤35/μm and ≤80μm, respectively, and the degree S of orientational concentration in the colony, represented by S=X20°/X30°, is regulated to ≤0.8, where X30° means the area of colonies where the orientation difference between adjacent crystalline grains is ≤30° and X20° means the area of colonies where the orientation difference between adjacent crystalline grains is ≤20°, among X30°. By this method, a wide range of application ranging from a dry cell inner package can, etc., to various household electrical and potential parts, automobile parts, etc., can be expected.;COPYRIGHT: (C)1998,JPO
展开▼
机译:解决的问题:通过规定含有特定基本成分的钢板的平均结晶粒径,并规定菌落的大小和程度,从而能够制造具有抗皱性和深冲性的罐用冷轧钢板。菌落中的定向浓度。 ;解决方案:一种钢,其成分包含以重量计0.0005-0.0150%的C,≤0.10%的Si,0.1-0.6%的Mn,P和S分别≤0.02%,0.015-0.15%的成分使用Al,N≤0.02%,余量为Fe,不可避免的杂质。此外,将平均结晶粒径(d)和平均菌落尺寸分别调节为≤35/μm和≤80μm,菌落中取向浓度的度S为S = X 20 Sub>°/ X 30 Sub>°调节至≤0.8,其中X 30 Sub>°表示相邻晶粒之间的取向差≤30°的菌落面积和X 20 Sub>°是指X 30 Sub>°中相邻晶粒间取向差≤20°的菌落面积。通过这种方法,可以期待从干电池内包装罐等到各种家用电气和潜在零件,汽车零件等的广泛应用。版权所有:(C)1998,日本特许厅
展开▼