Manufacturing method of silicon carbide ceramics having high fracture toughness
Manufacturing method of silicon carbide ceramics having high fracture toughness
展开▼
机译:具有高断裂韧性的碳化硅陶瓷的制造方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
The present invention relates to a method for producing silicon carbide ceramics having high fracture toughness, which is used for pickling rollers, bearings and the like, and is characterized in that titanium carbide (TiB2) Particles are added in an amount of 10 to 20% by volume, and at the same time, 2% by weight of carbon and 0.5% by weight of boron are added and mixed as a sintering aid, and then the mixture is mixed with an inert gas atmosphere at 1950C to 2050C (SiC) ceramics having a high fracture toughness by a process of sintering under a pressure of 300 kg / cm 2 .
展开▼
机译:本发明涉及具有高断裂韧性的碳化硅陶瓷的制造方法,其用于酸洗辊,轴承等,其特征在于,添加了碳化钛(TiB 2 Sub>)粒子。以10至20体积%的量,同时,加入2重量%的碳和0.5重量%的硼作为烧结助剂并混合,然后将该混合物与惰性气体气氛混合通过在300kg / cm 2的压力下进行烧结的方法,在1950℃至2050℃下具有高断裂韧性的(SiC)陶瓷。