摘要
The present invention relates to the production of high Ni-containing high alloy thick plate material for use in low temperature gas containers such as LNG; The purpose is to provide a continuous casting method for producing a 6-15% Ni-containing high alloy thick plate material, which is usually produced through the ingot-fragmentation process, by continuous casting.;The present invention for achieving the above object is a continuous casting method while injecting molten steel refined into the mold, the molten steel is molten steel for high alloy thick plate material containing 6-15% nickel; Casting rate is 0.8-1.0 m / min while injecting a flux for medium carbon having a basicity of 0.9-1.2 into the molten steel surface while adjusting the taper of the short side of the mold in the range of 1.05-1.10%; The technical gist of the method is to play a high nickel-containing high alloy thick plate material which is continuously cast with the secondary cooling ratio water poured into the bottom of the mold in the range of 0.40 to 0.45 l / kg.
展开▼
机译:本发明涉及用于诸如LNG之类的低温气体容器的高含镍高合金厚板材料的生产。目的是提供一种连续铸造方法,用于通过连续铸造来制造通常通过铸锭碎裂工艺来制造的6-15%的含Ni的高合金厚板材料。在将精炼的钢水注入到模具中的同时进行连续铸造的方法中,钢水是用于镍含量为6-15%的高合金厚板材料的钢水。铸造速度为0.8-1.0m / min,同时将碱度为0.9-1.2的中等碳的助熔剂注入钢水表面,同时将铸模短边的锥度调节在1.05-1.10%的范围内;该方法的技术要点是发挥高含镍高合金厚板材料的作用,该材料通过将二次冷却比水以0.40至0.45 l / kg的范围倒入模具底部的方式连续铸造。
展开▼