PREPARATION METHOD FOR LOW-TEMPERATURE-SINTERABLE -BASED PEROVSKITE DIELECTRIC POWDER
PREPARATION METHOD FOR LOW-TEMPERATURE-SINTERABLE -BASED PEROVSKITE DIELECTRIC POWDER
展开▼
机译:基于低温烧结的钙钛矿型介电粉的制备方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
The present invention is to mix PbO powder and Nb 2 O 5 powder; A solution in which soluble Mg 2+ is dissolved is added to the mixed powder slurry; Thereafter removing the solvent from the solution to obtain a PMN (Pb (Mg 1/3 Nb 2/3 ) O 3 ) precursor; Calcining the precursor powder at 800-950 ° C. and sintering the obtained powder; A method for producing a perovskite-based PMN dielectric comprising: a PbO powder and an Nb 2 O 5 powder; A solution in which soluble Mg 2+ is dissolved is added to the mixed powder slurry; Thereafter removing the solvent from the solution to obtain a PMN (Pb (Mg 1/3 Nb 2/3 ) O 3 ) precursor; Mixing PbTiO 3 powder with the PMN precursor and drying to obtain PMN-PT (0.9Pb (Mg 1/3 Nb 2/3 ) O 3 -0.1PbTiO 3 ) precursor; Calcining the precursor powder at 750 ° -950 ° C and sintering the powder obtained; And PbO powder, Nb 2 O 5 powder and TiO 2 powder; A solution in which soluble Mg 2+ is dissolved is added to the mixed powder slurry; Thereafter removing the solvent from the solution to obtain a PMN-PT precursor; Calcining the precursor powder at 800 ° -950 ° C. and sintering the obtained powder; Provided is a method for producing a perovskite-based PMN-PT dielectric.
展开▼
机译:本发明是将PbO粉末和Nb 2 Sub> O 5 Sub>粉末混合。将溶解有可溶性Mg 2 + Sup>的溶液添加到混合粉浆中;然后从溶液中除去溶剂以获得PMN(Pb(Mg 1/3 Sub> Nb 2/3 Sub>)O 3 Sub>)O。在800-950℃下煅烧前体粉末并烧结所得粉末;一种钙钛矿基PMN电介质的制造方法,包括:PbO粉末和Nb 2 Sub> O 5 Sub>粉末;将溶解有可溶性Mg 2 + Sup>的溶液添加到混合粉浆中;然后从溶液中除去溶剂以获得PMN(Pb(Mg 1/3 Sub> Nb 2/3 Sub>)O 3 Sub>)O。将PbTiO 3 Sub>粉末与PMN前体混合并干燥以获得PMN-PT(0.9Pb(Mg 1/3 Sub> Nb 2/3 Sub>)O 3 Sub> -0.1PbTiO 3 Sub>)前体;将前体粉末在750°-950°C下煅烧并烧结所得粉末;以及PbO粉,Nb 2 Sub> O 5 Sub>粉和TiO 2 Sub>粉;将溶解有可溶性Mg 2 + Sup>的溶液添加到混合粉浆中;然后从溶液中除去溶剂,得到PMN-PT前体。在800°-950°C下煅烧前驱体粉末并烧结所得粉末;提供了一种用于制造基于钙钛矿的PMN-PT电介质的方法。
展开▼