Method for producing cold rolled duplex stainless steel with extremely high strength and steel plate produced thereby
Method for producing cold rolled duplex stainless steel with extremely high strength and steel plate produced thereby
展开▼
机译:具有极高强度的冷轧双相不锈钢的生产方法和由此生产的钢板
展开▼
页面导航
摘要
著录项
相似文献
摘要
Cold-rolled and annealed steel sheet comprises (in wt.%): carbon (0.055-0.095); manganese (2-2.6); silicon (0.005-0.35); sulfur (= 0.005); phosphorus (= 0.05); aluminum (0.1-0.3); molybdenum (0.05-0.25); chromium (0.2-0.5); nickel (= 0.1); niobium (0.01-0.04); titanium (0.01-0.05); boron (0.0005-0.0025); and nitrogen (0.002-0.007), where the rest of the composition is iron and impurities. An independent claim is included for a process for preparation of the steel sheet comprising pouring the steel in the form of semi-product, carrying the semi-product at a temperature of 1150-1250[deg] C, hot rolling of the semi-finished product with a temperature of end-rolling of greater than argon (Ar3) to obtain a hot rolled product, coiling the hot-rolled at a temperature of 500-570[deg] C, cleaning the hot rolled product, making cold rolling with a reduction rate of 30-80% to obtain cold rolled product, heating the cold rolled product having a speed of 1-5[deg] C/s and annealing temperature including Ac1+40[deg] C-Ac3-30[deg] C , (where Ac1 is initial temperature of allotropic transformation, and Ac3 is final temperature of allotropic transformation) for 30-300 seconds to obtain a heated and annealed product with a structure comprising austenite and cooling the product to a temperature below the initial temperature of formation of martensite (M s) temperature with sufficient speed so that austenite is completely transformed to martensite.
展开▼