POLYPROPYLENE RESIN COMPOSITION FOR NON SLIP ON WOVEN BAG AND WOVEN BAG MANUFACTURED BY USING THE SAME
POLYPROPYLENE RESIN COMPOSITION FOR NON SLIP ON WOVEN BAG AND WOVEN BAG MANUFACTURED BY USING THE SAME
展开▼
机译:聚丙烯树脂防滑编织袋组成和编织袋的相同使用
展开▼
页面导航
摘要
著录项
相似文献
摘要
PURPOSE: A polypropylene-based resin composition for extrusion lamination is provided to have excellent processing rate and improved necking strength while obtaining improved incline coefficient. CONSTITUTION: A polypropylene-based resin composition includes: 75-85 parts by weight of polypropylene polymer manufactured by using a diether-based catalyst; 15-25 parts by weight of a low density polyethylene; and 0.05-1 parts by weight of a molecular weight-controlling master batch. The polypropylene polymer is a polypropylene homopolymer and has a melting temperature of 164C or less and a melting index of 10-20 g/10min(230C,2.16kgf). A melt index of the low density polyethylene is 8-30 g/10min(190C,2.16kgf) and a density thereof is 0.915 g/cm^cm^3 or less.
展开▼
机译:用途:提供用于挤出层压的聚丙烯类树脂组合物,以具有优异的加工速率和改善的颈缩强度,同时获得改善的倾斜系数。组成:一种聚丙烯基树脂组合物,包括:75-85重量份的使用二醚基催化剂制造的聚丙烯聚合物;和15-25重量份的低密度聚乙烯;和0.05-1重量份的控制分子量的母料。聚丙烯聚合物是聚丙烯均聚物,其熔融温度为164℃以下,熔融指数为10-20g / 10min(230℃,2.16kgf)。低密度聚乙烯的熔体指数为8-30g / 10min(190℃,2.16kgf),密度为0.915g / cm 2 / cm 3或更小。
展开▼