Water-based paint , and a method of manufacturing the same for anticorrosion treatment of seawater-resistant Hiroshi climate

摘要

The present invention relates to a process for the preparation and processing anticorrosion coatings construction parts Hiroshi climate. Aluminum zinc silicon alloy powder, an organic solvent, nano-oxide particles reinforcing agent, deionized water, binders, corrosion inhibitors, dispersing agents, and the coating comprises a thickener. Mixing ratio following the paint "aluminum zinc silicon alloy powder: organic solvents: nano-oxide particles reinforcing agent: deionized water: binder: corrosion inhibitors: dispersant: thickener = 30.0~50.0g: 10.0~25.0 It is formulated in 0.1~2.0g ": mL: 1.0~4.0g: 15.0~30.0mL: 2.0~5.0g: 1.0~3.0g: 0.1~2.0mL. The zinc aluminum silicon alloy powder, composed of the elements Al, Zn, etc. Si. None [Selection Figure]