HIGH-STRENGTH HEAT-TREATABLE ALUMINIUM ALLOY AND ARTICLE MADE THEREOF
HIGH-STRENGTH HEAT-TREATABLE ALUMINIUM ALLOY AND ARTICLE MADE THEREOF
展开▼
机译:高强度可热处理铝合金及其制品
展开▼
页面导航
摘要
著录项
相似文献
摘要
FIELD: metallurgy.;SUBSTANCE: alloy contains in wt %: zinc 8-10, magnesium 2.0-3.0, copper 1.6-2.6, scandium 0.12-0.25, zirconium 0.06-0.20, beryllium 0.0001-0.005, cobalt 0.05-0.15, nickel 0.5-1.0, iron 0.45-0.95, aluminium - rest, at that ratio between zinc and magnesium is within range 3.1-4.1.;EFFECT: increased alloy strength at room temperature, and creep resistance at moderately increased temperatures.;3 tbl, 1 ex
展开▼
机译:领域:冶金;物质:合金中的重量百分比:锌8-10,镁2.0-3.0,铜1.6-2.6,scan 0.12-0.25,锆0.06-0.20,铍0.0001-0.005,钴0.05-0.15,镍0.5 -1.0,铁0.45-0.95,铝-其余,锌和镁之间的比例在3.1-4.1范围内;效果:室温下合金强度增加,温度适度提高时的抗蠕变性。; 3 tbl,1 ex