The present invention relates to a celadon glaze powder, a frit and water, wherein the frit has a chemical composition of 54 to 64 wt% of SiO 2 , 5 to 10 wt% of Al 2 O 3, 10 to 18 wt% of CaO, A powder comprising 0.1 to 5% by weight of K 2 O, 0.01 to 2 % by weight of Na 2 O, 0.001 to 1.5% by weight of TiO 2 , 0.1 to 6% by weight of B 2 O 3 and 5 to 20% Wherein the celadon glaze powder and the frit are in a weight ratio of 60:40 to 95: 5 and have a water content of 35 to 55%, and a method for producing celecrosis improved in scratch resistance using the same . According to the present invention, a celadon glaze composition can be used to produce a celadon having improved scratch resistance.
展开▼
机译:青瓷釉粉,玻璃料和水本发明涉及一种青瓷釉粉,玻璃料和水,其中玻璃料的化学组成为SiO 2 <54%至64%(重量),Al 2 <5%至10%。 Sub> O 3, Sub> 10至18 wt%的CaO,一种粉末,包含0.1至5%重量的K 2 Sub> O,0.01至 2 < Na 2 Sub> O的/ Sub>重量百分比,TiO 2 Sub>的0.001至1.5重量%,B 2 Sub>的0.1至6%重量> O 3 Sub>和5至20%,其中青瓷釉粉和玻璃料的重量比为60:40至95:5,含水量为35至55%,用相同的方法生产的celecrosis的抗划伤性得到了改善。根据本发明,青瓷釉组合物可用于生产具有改善的耐刮擦性的青瓷。
展开▼