MONOPHASIC PMN-PT CERAMIC ELEMENT AND PRODUCTION METHOD THEREFOR
MONOPHASIC PMN-PT CERAMIC ELEMENT AND PRODUCTION METHOD THEREFOR
展开▼
机译:单相PMN-PT陶瓷元件及其生产方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
A novel partial covering method is disclosed for synthesizing pyrochlore free, stoichiometric and monophasic PMN-PT ceramics involving pelletizing a mixture of PbO, MgNb2O6, and TiO2 in the ratio 1:0.65:0.35 and subjecting the pelletized mixture to a modulated heat treatment cycle. The disclosure also relates to pyrochlore-free PMN-PT ceramic element having a saturation polarization (Psat) value of at least about 31.5 µC/cm2, a remanent polarization (Pr) value of at least about 24.7 µC/cm2, a reduced coercive field (Ec) value of at least about 6.1 kV/cm and squareness factor (Rsq) of at least about 1.10. The ceramic element has a piezoelectric property of at least 402 pC/N, a dielectric response of at least 11057 at 1kHz and a dielectric loss of less than about 0.062.
展开▼
机译:公开了一种新颖的部分覆盖方法,用于合成无烧绿石,化学计量和单相的PMN-PT陶瓷,包括将PbO,MgNb2O6和TiO2的比例为1:0.65:0.35的混合物造粒,并对造粒的混合物进行调制的热处理循环。本公开还涉及具有至少约31.5μC/ cm 2的饱和极化(Psat)值,至少约24.7μC/ cm 2的剩余极化(Pr)值,矫顽场减小的无烧绿石的PMN-PT陶瓷元件。 (Ec)值至少约为6.1 kV / cm,矩形系数(Rsq)至少约为1.10。陶瓷元件的压电性能至少为402 pC / N,在1kHz时的介电响应至少为11057,介电损耗小于约0.062。
展开▼