Polyethylene powder, method for its production and use in rotational molding
Polyethylene powder, method for its production and use in rotational molding
展开▼
机译:聚乙烯粉末,其生产方法和在滚塑中的用途
展开▼
页面导航
摘要
著录项
相似文献
摘要
Polyethylene powder comprising at least one additive having: Melt Flow Index (MFI), measured at 190° C. with a load of 2.16 kg in accordance with standard ISO 1133-1:2011, ranging from 0.1 g/10 minutes to 100 g/10 minutes, preferably ranging from 5 g/10 minutes to 35 g/10 minutes; density ranging from 0.890 g/cm3 to 0.965 g/cm3, preferably ranging from 0.940 g/cm3 to 960 g/cm3; bulk density ranging from 0.35 g/cm3 to 0.60 g/cm3, preferably ranging from 0.40 g/cm3 to 0.50 g/cm3; average particle diameter (d50) ranging from 400 μm to 800 μm, preferably ranging from 450 μm to 780 μm. Said polyethylene powder comprising at least one additive can be advantageously used in rotomolding.
展开▼
机译:包含至少一种添加剂的聚乙烯粉末,该添加剂具有:熔体流动指数(MFI),根据标准ISO 1133-1:2011在190°C下以2.16 kg的载荷测量,范围为0.1 g / 10分钟至100 g / 10分钟,优选5g / 10分钟至35g / 10分钟;密度为0.890g / cm 3至0.965g / cm 3,优选为0.940g / cm 3至960g / cm 3;堆积密度为0.35g / cm 3至0.60g / cm 3,优选为0.40g / cm 3至0.50g / cm 3;平均粒径(d50)为400μm至800μm,优选为450μm至780μm。所述包含至少一种添加剂的聚乙烯粉末可有利地用于滚塑中。
展开▼