Ni, Co, Fe and Co/Cu multilayered nanowires were electrodeposited into a nano-well template to synthesize novel functional ferromagnetic devices. Growth rate of Co/Co multilayered nanowires was around 40 nm·sec-1 and the cylindrical shape was precisely transferred from the nanochannels to the nanowires and the aspect ratio reached up to ca. 150. Magnetic hysteresis loops of Ni, Co and Fe nanowires with diameter 40 nm showed typical perpendicular magnetization behavior due to the uni-axial shape anisotropy and the coercive force reached up to around 1 kOe. 2% of anisotropic magnetoresistance effect was observed in Ni nanowires electrodeposited into anodized aluminum oxide template, while 20% of giant magnetoresistance effect was observed in Co/Cu multilayered nanowires.