Magnetic behavior of Sm-Co-based permanent magnets during order/disorder phase transformations

摘要

The structural transformation from the metastable disordered TbCu7-type SmCo7 structure to the equilibrium ordered Th2Zn17-type Sm2Co17 structure was revealed by x-ray diffraction analysis using Reitveld refinement. The magnetic properties depended strongly on the stage of the transformation, as the coercivity strongly depended on the annealing temperature. The as-solidified alloy in the TbCu7-type structure had a coercivity of 4 kOe, which increased to greater than 9 kOe. The coercivity decreased to around 5 kOe as the transformation neared completion upon annealing at higher temperatures. The magnetization processes were also strongly influenced by the structural state. Initially it was totally controlled by nucleation followed by the domain wall pinning-controlled magnetization process.