Spacer layer effect and microstructure on multi-layer NdFeB/Nbn films

机译:多层NdFeB / Nb n薄膜的隔离层效应和微观结构

代理获取
本网站仅为用户提供外文OA文献查询和代理获取服务,本网站没有原文。下单后我们将采用程序或人工为您竭诚获取高质量的原文,但由于OA文献来源多样且变更频繁,仍可能出现获取不到、文献不完整或与标题不符等情况,如果获取不到我们将提供退款服务。请知悉。

摘要

[[abstract]]Spacer layer effect on multi-layer [NdFeB/Nb]n films has been investigated from the variation of magnetic properties and microstructure of the films. From a HRTEM cross-section view observation, the average grain size of [NdFeB/Nb]n multi-layers was controlled by both annealing temperature and thickness of NdFeB layer. Selected area diffraction pattern indicated that the structure of Nb spacer layer was amorphous. The grain size and coercivity of [NdFeBx/Nb]n films change from 50 nm and 16.7 kOe to 167 nm and 9 kOe for films with x = 40 nm, n = 10 and x = 200 nm, n = 2, respectively.
机译:从[NdFeB / Nb] n多层薄膜的磁性和微观结构的变化,研究了其对多层[NdFeB / Nb] n薄膜的影响。从HRTEM横截面观察,[NdFeB / Nb] n多层的平均晶粒尺寸通过退火温度和NdFeB层的厚度来控制。选定的区域衍射图表明Nb间隔层的结构是非晶的。对于x = 40 nm,n = 10和x = 200 nm,n = 2的薄膜,[NdFeBx / Nb] n薄膜的晶粒尺寸和矫顽力分别从50 nm和16.7 kOe变为167 nm和9 kOe。

著录项

  • 作者

    TsaiJai-Lin;

  • 作者单位
  • 年度 2011
  • 总页数
  • 原文格式 PDF
  • 正文语种 [[iso]]en
  • 中图分类

相似文献

  • 外文文献
  • 中文文献
  • 专利

客服邮箱:kefu@zhangqiaokeyan.com

京公网安备:11010802029741号 ICP备案号:京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有
  • 客服微信

  • 服务号