The effect of resin matrix composition on mechanical properties of e-glass fiber-reinforced composite for dental use

摘要

The effects of resin matrix composition including bis-phenol-A-diglycidyl dimethacrylate (bis-GMA)-methyl methacrylate (MMA) based or urethane dimethacrylate (UEDMA)-triethylene glycol dimethacrylate (TEGDMA) based composition and storage conditions on the mechanical properties of E-glass fiber-reinforced composites (FRCs) were studied. Three experimental groups ('Exper 1', 'Exper 2', 'Exper 3') with differing UEDMA to TEGDMA ratio in the matrix together with a control group ('Control') based on bis-GMA-MMA resin matrix were prepared by light-curing. The storage conditions for each group were dry storage at room temperature for 24 h and 30- and 60-day immersion in deionized (DI) water at 37°C, which further divided each group into three subgroups. For all the four composition groups, mechanical properties including hardness, flexural strength and modulus in both three-point and four-point bendings were tested (n = 6), together with water sorption and solubility study (n = 6) and fracture site scanning with a scanning electron microscope (SEM). The experimental specimens were relatively strong and stiff in three-point bending compared to previous research. The same specimens in three-point bending had a lower flexural modulus and fractured at higher flexural stress than in four-point bending. According to the SEM images after fracture, some resin matrix was still bound to the fiber surface, showing cohesive-interfacial fracture type and relatively stable matrix-fiber adhesion. According to comprehensive analysis, the control group showed superior mechanical performance in most of the tests.