Temperature rise and initial shrinkage of alkali-activated fly ash cement pastes

摘要

This paper reports on core temperature development and initial shrinkage of fly ash cement pastes activated withsodium hydroxide solution at different concentrations during elevated-temperature curing at 60°C. The results indicatethat a high sodium hydroxide concentration might result in a substantial rise in the core temperature of samples,dependent on the mould size and ratio of paste to oven volume. An increase in alkali concentration was also found toincrease the initial shrinkage of the pastes during elevated-temperature curing. Excessive initial shrinkage andtemperature increase might lead to the appearance of internal stresses in the pastes, which can affect the materialperformance.