Photoluminescence and thermoluminescence studies of Mg 2 SiO 4 :Eu 3+ nano phosphor

摘要

Nanoparticles of Eu 3+ doped Mg 2 SiO 4 are prepared using low temperature solution combustion technique with metal nitrate as precursor and urea as fuel. The synthesized samples are calcined at 800 °C for 3 h. The Powder X-ray diffraction (PXRD) patterns of the sample reveled orthorhombic structure with α-phase. The crystallite size using Scherer's formula is found to be in the range 50–60 nm. The effect of Eu 3+ on the luminescence characteristics of Mg 2 SiO 4 is studied and the results are presented here. These phosphors exhibit bright red color upon excitation by 256 nm light and showed the characteristic emission of the Eu 3+ ions. The electronic transition corresponding to 5 D 0 → 7 F 2 of Eu 3+ ions (612 nm) is stronger than the magnetic dipole transition corresponding to 5 D 0 → 7 F 1 of Eu 3+ ions (590 nm). Thermoluminescence (TL) characteristics of γ-rayed Mg 2 SiO 4 :Eu 3+ phosphors are studied. Two prominent and well-resolved TL glows with peaks at 202 °C and 345 °C besides a shoulder with peak at ∼240 °C are observed. The trapping parameters-activation energy ( E ) , order of kinetics ( b ) and frequency factor ( s ) are calculated using glow curve shape method and the results obtained are discussed.