>Fabrication of high infrared reflective ceramic films on polyester fabrics by RF magnetron sputtering
【2h】
Fabrication of high infrared reflective ceramic films on polyester fabrics by RF magnetron sputtering
展开▼
机译：射频磁控溅射在聚酯织物上制备高红外反射陶瓷膜
展开▼
免费
页面导航
摘要
著录项
引文网络
相似文献
相关主题
摘要
In this project, AZO/Ag/AZO and AZO/Cu/AZO multilayer films were deposited on polyester fabrics with radio frequency (RF) magnetron sputtering technology. The prepared samples were systematically investigated with X-ray diffraction (XRD), Scanning Electron Microscope (SEM) and Fourier Transform Infrared Spectroscopy. Physical properties of the coated fabrics were evaluated by infrared reflection rate, contact angle (CA), air permeability and UPF value. The results indicated that the AZO/Ag/AZO coated polyester fabrics presented a high infrared reflection rate of 95-96% and CA of about 92.5¢X/93.5¢X, air permeability of 17.1/15.4 ml/s/cm2 at 100 Pa and UPF values of 40.64/46.67. The AZO/Cu/AZO coated polyester fabrics exhibited an infrared reflection rate of 50-60%, CA of about 88¢X/88.5¢X, air permeability of 18.1/17.5 ml/s/cm2 at 100 Pa and UPF values of 41.96/48.437.
展开▼
机译：在该项目中，采用射频（RF）磁控溅射技术将AZO / Ag / AZO和AZO / Cu / AZO多层膜沉积在聚酯织物上。使用X射线衍射（XRD），扫描电子显微镜（SEM）和傅里叶变换红外光谱对系统制备的样品进行了系统研究。通过红外反射率，接触角（CA），透气性和UPF值评估涂层织物的物理性能。结果表明，AZO / Ag / AZO涂层聚酯织物在100 Pa下表现出95-96％的高红外反射率和92.5¢X / 93.5¢X的CA，透气度为17.1 / 15.4 ml / s / cm2。和UPF值分别为40.64 / 46.67。涂有AZO / Cu / AZO的聚酯织物在100 Pa下的红外反射率为50-60％，CA为约88¢X / 88.5¢X，透气度为18.1 / 17.5 ml / s / cm2，UPF值为41.96。 /48.437。
展开▼