Influence of the Amount of Master Alloy on the Properties of Austenitic Stainless Steel AISI 316L Powder Sintered in Hydrogen

机译:中间合金量对氢烧结奥氏体不锈钢AISI 316L粉末性能的影响。

代理获取
本网站仅为用户提供外文OA文献查询和代理获取服务,本网站没有原文。下单后我们将采用程序或人工为您竭诚获取高质量的原文,但由于OA文献来源多样且变更频繁,仍可能出现获取不到、文献不完整或与标题不符等情况,如果获取不到我们将提供退款服务。请知悉。

摘要

AISI 316L austenitic stainless steel powder was modified with four different amounts of boron (0.1; 0.2; 0.3; 0.4 of wt. %) in the form of MasterAlloy micro-powder, and was sintered in a pure dry hydrogen atmosphere in order to obtain high density sintered samples characterized by a thickened non-porous surface layer. We investigated the influence of the amount of boron on: density, hardness, grain microhardness, porosity, microstructure and surface quality. The study revealed that it is possible by a conventional compacting and sintering process to obtain near full-density sintered samples with a non-porous superficial layer without boride precipitations.
机译:AISI 316L奥氏体不锈钢粉末用MasterAlloy微粉形式的四种不同量的硼(0.1; 0.2; 0.3; 0.4重量%)进行改性,并在纯干燥氢气气氛中烧结以获得较高的高密度烧结样品,其特征在于无孔表面层增厚。我们研究了硼含量对密度,硬度,晶粒显微硬度,孔隙率,显微组织和表面质量的影响。研究表明,通过常规的压实和烧结工艺可以获得具有无孔表面层且无硼化物沉淀的接近全密度的烧结样品。

著录项

  • 作者

    Skaloń Mateusz; Kazior Jan;

  • 作者单位
  • 年度 2017
  • 总页数
  • 原文格式 PDF
  • 正文语种 eng
  • 中图分类

相似文献

  • 外文文献
  • 中文文献
  • 专利
代理获取

客服邮箱:kefu@zhangqiaokeyan.com

京公网安备:11010802029741号 ICP备案号:京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有
  • 客服微信

  • 服务号