This research to investigate the characteristics of wood pellets from wood rubber waste as alternative renewable energy sources and determine the best treatment. This research was conducted in experiments with completely randomized design (CRD), which consists of three treatments three replications, with the use of wood rubber waste, tapioca flour and water as well as the tools use are peletmill, calory meter combustion bomb, hammermill, oven, container, stirrer, weigher, measure cups, stopwach, wood pellets stove and camera. It can be concluded that the water content wood pellet 15,06% - 17,26%, wood pellet density 0,408 g/cm3 (408 kg/m3) – 0,628 g/cm3 (628 kg/m3), long burn wood pellets 5,42 minutes/200gr – 7,29 minutes/200gr and a calorific value 4029 Kcal/kg - 4106 Kcal/kg. Treatment to three with tapioca powder rubber wood + 30% + 300 ml water have the appropriate or best treatment approach by SNI, where the water content of 15,06%, density of 0,628 g/cm3 (628 kg/m3), long burning 5,42 minutes/200gr and calorific value of 4106 Kcal/kg.
展开▼
机译：这项研究旨在调查以木橡胶废料作为替代可再生能源的木屑颗粒的特性，并确定最佳处理方法。这项研究是在具有完全随机设计（CRD）的实验中进行的，该设计包括三种处理方式，一式三份重复使用木橡胶废料，木薯粉和水，并使用了Peletmill，卡路里燃烧弹，锤磨机，烤箱，容器，搅拌器，秤，量杯，咖啡壶，木质颗粒炉和照相机。可以得出结论，木质颗粒的含水量为15,06％-17,26％，木质颗粒密度为0,408 g / cm3（408 kg / m3）– 0,628 g / cm3（628 kg / m3），长燃木质颗粒5 ，42分钟/ 200gr – 7,29分钟/ 200gr，发热量4029 Kcal / kg-4106 Kcal / kg。用木薯粉橡胶木+ 30％+ 300毫升水处理3种具有SNI适当或最佳的处理方法，其中水含量为15,06％，密度为0,628 g / cm3（628 kg / m3），长时间燃烧5,42分钟/ 200gr，发热量4106 Kcal / kg。
展开▼