Mechanical and Thermo-Physical Characterization of Three-Directional Carbon Fiber Composites for W-7X and ITER

摘要

Carbon fiber composites (CFCs) are the first choice as plasma facing materials for the strike points of divertor targets for future nuclear fusion devices like WENDELSTEIN 7-X and ITER. For the application in these facilities several potential European 3D-CFCs were compared and qualified: (I) four material batches of NB31 produced by Snecma Propulsion Solide (SNECMA); (2) NB41, SNECMA, the upgraded version of NB31: (3) N31, SNECMA, which is densified by chemical vapor infiltration (CVI) instead of a final liquid pitch infiltration characteristic for NB31; (4) a new developmental 3D-CFC produced by DUNLORThe characterization of the composites is comprised of thermo-physical measurements and tensile tests. The results are correlated to density and microstructure and summarized as follows: (I) NB41 provides the highest thermal conductivity in the ex-pitch direction of similar to 375 W/(m K)at room temperature; (2) all material grades are, due to their heterogeneity, characterized by a relatively large scatter of mechanical properties: (3) the different densification process for N31 in comparison to NB31 has no influence on the material properties; (4) NB41 provides in all three directions a comparably high tensile strength with an average in the ex-pitch direction of similar to 220 MPa; (5) the 3D-CFC from DUNLOP is comparable to NB41 but yet does not meet the specifications in the needling direction. (C) 2008 Elsevier B.V. All rights reserved.