Surface Corrosion of Mg-Containing Al-BAsed Alloys

摘要

During heat-treatment of Mg-containing Al-based alloys, the Mg concentration changes considerably. As compared to the pure material significant surface corrosion is observed for the air heattreated alloy. In vacuum heat treatment the Mg content of the surface layer increases considerably. Initially metallic Mg is detected on the surface which, however, becomes oxidized later on. On the basis of the investigations one has to assume that the process is not a simple diffusion mechanism only. A new conception is formed for the process according to which it is controlled by the breaking up of the Al2O3 barrier layer by Mg. | Während einer Wärmebehandlung von Mg enthaltenden Al-Legierungen ändert sich die Mg-Konzentration beträchtlich. Im Vergleich zu dem reinen Material wird eine signifikante Oberflächenkorrosion für in Luft getemperte Legierungen beobachtet. Bei Vakuumtemperung steigt der Mg-Gehalt der Oberflächenschicht beträchtlich an. Anfangs wird metallisches Mg auf der Oberfläche nachgewiesen, das jedoch später oxidiert wird. Auf der Grundlage der Untersuchungen muß angenommen werden, daß der Prozess nicht nur ein einfacher Diffusionsmechanismus ist. Eine neue Vorstellung für den Prozeß wird vorgeschlagen, derzufolge dieser Prozeß durch das Aufbrechen der Al2O3-Barrierenschicht durch Mg gesteuert wird.