Thermal conductivity and thermal cyclic fatigue of multilayered Gd2Zr2O7/YSZ thermal barrier coatings processed by suspension plasma spray

摘要

Rare earth zirconates have lower thermal conductivity, better phase stability, improved sintering resistance and CMAS (calcium magnesium alumino silicates) infiltration resistance than yttria stabilized zirconia (YSZ) at temperatures above 1200 °C. However, their lower fracture toughness and lower coefficient of thermal expansion (CTE) compared to YSZ lead to premature coating failure. In order to overcome these drawbacks at higher temperatures, a multilayered coating approach is attempted in this study and compared with the single layer YSZ. Suspension plasma spray of single layer YSZ, single layer gadolinium zirconate (GZ) and double layer GZ/YSZ was carried out. Additionally, a triple layer coating system, with denser gadolinium zirconate on top of the GZ/YSZ system was sprayed to impart an added functionality of sealing the TBC from CMAS infiltration. Microstructural analysis was done using scanning electron microscopy and optical microscopy. Columnar microstructure with vertical cracks was observed. XRD analysis was used to identify phases formed in the as sprayed TBC samples. Porosity measurements were done using water impregnation method. Thermal diffusivity of single and multi-layered coatings was obtained by laser flash analysis and thermal conductivity of the coating systems was determined. It was found that the thermal conductivity of single layer gadolinium zirconate was lower than YSZ and that the thermal conductivity of multilayered systems were between their respective single layers. The single (YSZ), double (GZ/YSZ) and triple (GZ dense/GZ/YSZ) layer TBCs were subjected to thermal cyclic fatigue (TCF) test at 1100 °C and 1200 °C. It was observed that the single layer YSZ had lowest TCF life whereas the triple layer TBC had highest TCF life irrespective of test temperature.