A life study of AISI M-50 and Super Nitralloy spur gears with and without tip relief

摘要

Tests were conducted at 170 F with groups of 3.5-in.-pitch-diameter spur gear with and without tip relief made of consumable-electrode vacuum melted (CVM) Spur Nitralloy (5Ni-2Al) and CVM AISI M-50 steel. The AISI M-50 gears without tip relief had lives approximately 50 percent longer than the Super Nitralloy gears without tip relief. However, the Super Nitralloy gears with tip relief had lives equal to the AISI M-50 gears without tip relief. The difference in lives were not statistically significant. All gears failed by classical pitting fatigue at the pitch circle. However, the AIAI M-50 gears with tip relief failed by tooth fracture. AISI M-50 gear sets without tip relief having a spalled gear tooth which were deliberately overrun after spalling had occurred, failed by tooth fracture.